A change in laminate thickness due to terminating internal plies acts as a stress riser for both intralamina and interlaminar stresses. This laminate configuration is referred to as a ply drop. The linear elastic, three-dimensional stress distributions in the vicinity of a ply drop are determined for a graphite-epoxy laminate subject to axial tension and compression by a finite element analysis. It is shown that the interlaminar stresses have a maximum magnitude at the ply drop-off, and decrease proceeding away from the drop-off. Two modes of failure initiation are analyzed. In the pure resin regions surrounding the dropped plies, the maximum stress criterion is assumed to govern failure. The Tsai-Wu criterion is used for intralamina failure prediction. The influence of two laminate lay-ups and a variety of ply drop geometries on the response and failure are presented. / M.S.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/91127 |
| Date | January 1985 |
| Creators | Kemp, Brian Lee |
| Contributors | Aerospace and Ocean Engineering |
| Publisher | Virginia Polytechnic Institute and State University |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Thesis, Text |
| Format | v, 70 leaves, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 13131190 |