Recently, the rate of corrosion of copper water pipes in Bowling Green, Kentucky has unexpectedly accelerated. The specific reasons for this are unknown. Our aim is to elucidate the factors enhancing the corrosion and help understand the primary mechanisms of action. This will help in combating and reducing future corrosion incidents leading to pipe failure, thus reducing losses experienced when these pipes are replaced. This study seeks to explore the characteristics and factors involved. The scanning electron microscopy was used to obtain elemental composition, and images of both inside and outside of the corroded pipes. Strikingly, corrosion primarily occurred on the outside of the pipes, not inside. X-ray crystallography also was used to examine the pipes. The results showed that the interior of the pipes mostly consisted of SiO2, CuO2, CaCO3 while the exterior consisted of Cu2(OH)2CO3, Fe2Al2O4, CaCO3, SiO2 and Cu2O. There was no clear single factor for the corrosion observed. For further studies, we plan to long temporal experiments. The results from the study will help in minimizing the costs to the city in Bowling Green, Kentucky.
| Identifer | oai:union.ndltd.org:WKU/oai:digitalcommons.wku.edu:theses-2553 |
| Date | 01 October 2015 |
| Creators | Alghamdi, Reema M |
| Publisher | TopSCHOLAR® |
| Source Sets | Western Kentucky University Theses |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Masters Theses & Specialist Projects |
Page generated in 0.0019 seconds