One-dimensional (1D) nanostructures (NSs) of Zinc Oxide (ZnO) such as nanorods (NRs) have recently attracted considerable research attention due to their potential for the development of optoelectronic devices such as ultraviolet (UV) photodetectors and light-emitting diodes (LEDs). The potential of ZnO NRs in all these applications, however, would require synthesis of high crystal quality ZnO NRs with precise control over the optical and electronic properties. It is known that the optical and electronic properties of ZnO NRs are mostly influenced by the presence of native (intrinsic) and impurities (extrinsic) defects. Therefore, understanding the nature of these intrinsic and extrinsic defects and their spatial distribution is critical for optimizing the optical and electronic properties of ZnO NRs. However, identifying the origin of such defects is a complicated matter, especially for NSs, where the information on anisotropy is usually lost due to the lack of coherent orientation. Thus, the aim of this thesis is towards the optimization of the lowtemperature solution-based synthesis of ZnO NRs for device applications. In this connection, we first started with investigating the effect of the precursor solution stirring durations on the deep level defects concentration and their spatial distribution along the ZnO NRs. Then, by choosing the optimal stirring time, we studied the influence of ZnO seeding layer precursor’s types, and its molar ratios on the density of interface defects. The findings of these investigations were used to demonstrate ZnO NRs-based heterojunction LEDs. The ability to tune the point defects along the NRs enabled us further to incorporate cobalt (Co) ions into the ZnO NRs crystal lattice, where these ions could occupy the vacancies or interstitial defects through substitutional or interstitial doping. Following this, high crystal quality vertically welloriented ZnO NRs have been demonstrated by incorporating a small amount of Co into the ZnO crystal lattice. Finally, the influence of Co ions incorporation on the reduction of core-defects (CDs) in ZnO NRs was systematically examined using electron paramagnetic resonance (EPR).
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-141753 |
Date | January 2017 |
Creators | Alnoor, Hatim |
Publisher | Linköpings universitet, Fysik och elektroteknik, Linköpings universitet, Tekniska fakulteten, Linköping |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Linköping Studies in Science and Technology. Dissertations, 0345-7524 ; 1871 |
Page generated in 0.0016 seconds