Durability of the composite materials in marine environments has been investigated experimentally and with analytical and numerical methods. The main focus of this study is on the integrity of the fiber/matrix interface under seawater exposure. A single-fiber compression test specimen called the Outwater-Murphy (OM) test has been analyzed using mechanics of materials principles and linear elastic fracture mechanics. Sizing of the OM specimen was conducted so that debonding of the fiber from the interface should be achieved prior to yielding of the matrix and global instability failure. Stress analysis of the OM specimen has been conducted from theory of elasticity and finite element analysis. A superelement technique was developed for detailed analysis of the stress state at the fiber/matrix interface. The interface stress state at the debond site in the OM specimen, i.e. at the hole edge, was identified as biaxial tension at the fiber/matrix interface. Characterization of cure and post-cure of 8084 and 510A vinlyester resins has been performed using cure shrinkage tests based on dynamic mechanical analysis and coated beam experiments. In addition, moisture absorption, swelling and the influence of moisture on the mechanical properties of the resins were determined. Testing of OM specimens consisting of a single carbon or glass fiber embedded in vinylester resin at dry conditions and after seawater exposure revealed that the debond toughness was substantially reduced after exposure of the OM specimen to seawater. C(F) did not debond. Macroscopic carbon/vinylester woven composites where the fibers were sized with F sizing were tested in shear at dry conditions and after four weeks of seawater exposure. The shear strength was very little affected after the short immersion time. / by Muhammad Umar Farooq. / Thesis (Ph.D.)--Florida Atlantic University, 2009. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2009. Mode of access: World Wide Web.
| Identifer | oai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_3474 |
| Contributors | Farooq, Muhammad Umar., College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering |
| Publisher | Florida Atlantic University |
| Source Sets | Florida Atlantic University |
| Language | English |
| Detected Language | English |
| Type | Text, Electronic Thesis or Dissertation |
| Format | xx, 155 p. : ill. (some col.), electronic |
| Rights | http://rightsstatements.org/vocab/InC/1.0/ |