Includes bibliographical references (leaves 124-127). / Hydrogen was used as a temporary alloying element in CP Ti and Ti-6AI-4V. The microstructural evolution and phase transformations were monitored, before, during and after hydrogenation with in-situ dilatometric testing. Wrought CP Ti and Ti-6AI-4V specimens were pre-annealed and experienced four consecutive thermal cycles (Cycles 1-4) i.e. hydrogenation, post-hydrogenation, dehydrogenation and post-dehydrogenation, during dilatometric testing. The specimen in each thermal cycle was heated to 1000°C, heating rate 1°C/min (with an isothermal hold at 1000°C for three hours for hydrogenation and dehydrogenation cycles) and then cooled to room temperature at cooling rate of 1°C/min.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:uct/oai:localhost:11427/12339 |
| Date | January 2011 |
| Creators | Abbas, Naseeba |
| Contributors | Knutsen, Robert D |
| Publisher | University of Cape Town, Faculty of Engineering and the Built Environment, Centre for Materials Engineering |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Master Thesis, Masters, MSc |
| Format | application/pdf |
Page generated in 0.0098 seconds