Influência do tratamento térmico de alívio de tensões assoaciado à elevada energia de soldagem na tenacidade da zona termicamente afetada de um aço TMCP microligado aplicado em estruturas off-shore

Made available in DSpace on 2014-06-11T19:27:11Z (GMT). No. of bitstreams: 0
Previous issue date: 2011-05-02Bitstream added on 2014-06-13T18:55:39Z : No. of bitstreams: 1
lima_cas_me_guara.pdf: 1618894 bytes, checksum: 6e9dc3f3d8a6ae02d3aa4262c6d6f0c7 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Foi realizada a soldagem de chapas-teste de um aço API 2W 50, fabricado pelo processamento TMCP (Thermo-Mechanical Controlled Processing), sem resfriamento acelerado, com o processo de soldagem SAW-Tandem, com elevada energia de soldagem (4,0 kJ/mm), com a finalidade de aumento de produtividade, e aplicado o tratamento térmico de alívio de tensões (TTAT). Os resultados obtidos demonstraram que o TTAT associado à elevada energia de soldagem não promoveram variações significativas na microestrutura, na microdureza e nas tenacidades ao impacto (Charpy-V) e à fratura (CTOD). No entanto, os resultados de CTOD da ZTA foram baixos devido ao fato da ponta da trinca não estar localizada totalmente na ZTA; um volume significativo de metal de solda, de baixa tenacidade à fratura, foi revelado ao longo da extensão da trinca. As características do ciclo termomecânico do processamento TMCP (endurecimento por refino de grão e por aumento na densidade de discordâncias) foram as causas determinantes para a obtenção dos bons resultados de tenacidade no metal base e na ZTA, em condições de elevada energia de soldagem e de TTAT / It was done the welding of the samples of a steel API 2W 50, manufactured by TMCP process, without accelerated cooling, with SAW-Tanden process, with high heat input (4,0 kJ/mm), with goal to increase the productivity, and applied a PWHT. The results showed that the PWHT associated to high heat input didn´t promove significative changes in the microestructure, in the microhardness (HV0,2) and in the impact (Charpy-V) and fracture toughness (CTOD). However, the results of the CTOD in HAZ were low due to the fact the crack tip wasn´t localized fully in HAZ; a considerable volume of the weld metal, of the low toughness, was reveled in the extension of the crack. The characteristics of the thermomechanical cicle of TMCP process (strengthening by grain refinemment and by increasing in dislocations density) were the causes determinants to getting the good results of toughness in base metal and HAZ, in conditions of the high heat input and PWHT

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/94433
Date02 May 2011
CreatorsLima, Carlos Augusto Silveira [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Guimarães, Valdir Alves [UNESP], Bracarense, Alexandre Queiroz [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format110 f. : il.
SourceAleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation-1, -1, -1

Page generated in 0.0025 seconds