Oligomers of soft and hard segments of unsaturated polyesters (UPE) were synthesized in two steps of esterification. For the hard segment, isophthalic acid was first reacted with 1,2-propanediol, then maleic anhydride was added for further esterification. For the soft segment, diethylene glycol was used to replace 1,2-propanediol. Oligomers of soft and hard segments were blended in different ratios, and then cured with various amount of styrene. Dynamic mechanical and the stress-strain properties of these cured UPEs were evaluated. The results indicated that both stress and strain were above the criteria of the inhibitors when the amount of hard segment oligomer was 30, 60 or 70 wt% of UPE, and the added styrene was 35 or 45 phr relative to UPE. The formula of 30 wt% hard segment, 70 wt% soft segment, and 45 phr styrene was selected for the following studies.
Tetraethyl orthosilicate (TEOS) and poly(dimethyl siloxane) were incorporated into the uncured UPE resins via sol-gel process. Then fillers and 5, 10, 15, 20 or 30 wt% of magnesium hydroxide were blended with UPE resins and cured. Self-extinguished phenomenon was observed in the erosion tests when the amount of magnesium hydroxide was equal or higher than 15 wt% relative to UPE. After 101 days of nitroglycerin migration experiments, the migration rate and amount were significantly reduced for these filled specimens compared with the current formula of inhibitors.
In addition, 2.5 or 5 phr of phenyl triethoxysilane (PhTES) relative to UPE was added together with TEOS to study the physical properties of the organic-inorganic hybrid materials. When the amount of PhTES was 2.5 phr, it was found that the miscibility between inorganic and organic components improved, and their stress- strain properties also satisfied the criteria of the inhibitors.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0707106-033904 |
| Date | 07 July 2006 |
| Creators | Tsai, Shang-shun |
| Contributors | Ming Chen, Feng-Er Yu, shih-jung Bai, Jin-Long Hong |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0707106-033904 |
| Rights | off_campus_withheld, Copyright information available at source archive |