Previous issue date: 2014-04-02 / Capes / As peneiras moleculares mesoporosas possuem um arranjo hexagonal de
mesoporos com diâmetros de poros que variam de 2 a 10 nm, possuindo assim uma
área superficial elevada. A adição de um metal a sua estrutura tem como função
gerar a acidez ao material o tornando mais reativo, aumentado assim a possibilidade
do seu uso como catalisador na indústria do petróleo. Atualmente, um dos
problemas encontrados pelos pesquisadores para obtenção desse tipo de peneira, é
o longo tempo de formação das estruturas. No presente trabalho as peneiras
moleculares mesoporosas MCM-41 e Al-MCM-41 foram sintetizadas utilizando dois
processos hidrotermais, a tradicional e por micro-ondas, com o objetivo principal de
reduzir o tempo de síntese do material. A peneira molecular MCM-41 foi sintetizada
utilizando o processo hidrotermal tradicional, 100 oC por 48 horas , como também
utilizando o processo hidrotermal de micro-ondas através de três metodologias,
adotando diferentes tempos e temperaturas. Tomando como base os resultados
obtidos com as sínteses da peneira molecular MCM-41 por meio do método
hidrotermal de micro-ondas, os mesmos métodos foram aplicados para a peneira
molecular Al-MCM-41 nas mesmas condições de tempo e temperatura. Através dos
difratogramas foi possível perceber que a estrutura hexagonal foi formada. Verificouse
que o melhor tempo de síntese da Al-MCM-41 se deu com 60 minutos a 130 oC.
A partir destes dados, foram realizadas novas sínteses, reduzindo o tempo
gradativamente. Os resultados das análises de DRX, MEV e FTIR comprovam que
as peneiras moleculares mesoporosas foram formadas, sendo possível identificar
sua estrutura e morfologia. Os melhores resultados de síntese para as peneiras
moleculares mesoporosas MCM-41 e Al-MCM-41, foram nos tempos 60 e 40
minutos e temperatura de 130 oC, respectivamente. / The mesoporous molecular sieves have a hexagonal arrangement of
mesopores with pore diameters ranging from 2 to 10 nm, which implies in a high
surface area. The addition of a metal into these structures has the function of
generating acidity in the material making it more reactive, increasing the possibility of
using it as a catalyst into the oil industry. Nowadays, one of the problems found by
researches to obtain these type of molecular sieves is the long time of structure
formation taken by these materials. In this study, the mesoporous molecular sieves
MCM - 41 and Al -MCM -41 were synthesized using two traditional microwave, with
the primary goal of reducing the time of synthesis of the material hydrothermal
processes. The molecular sieve MCM -41 was synthesized using the traditional
hydrothermal process 100 °C for 48 hours , as well as hydrothermal process using
microwave by three methods , adopting different times and temperatures . Based on
the results obtained with the synthesis of molecular sieve MCM -41 by hydrothermal
microwave method, the same methods were applied to the molecular sieve Al -MCM
-41 under the same conditions of time and temperature. Through the DRX patterns
was observed that the hexagonal structure was formed. It was found that the best
time of synthesis of Al- MCM-41 was given 60 minutes at 130 oC. From these data,
new syntheses were carried out by reducing the time gradually. The results of DRX,
MEV and FTIR show that the mesoporous molecular sieves were formed, it is
possible to identify their structure and morphology. The best results for the synthesis
of mesoporous molecular sieves MCM - 41 and Al -MCM -41, were at times 60 and
40 minutes and temperatures of 130 °C, respectively.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/527 |
| Date | 30 April 2018 |
| Creators | MEDEIROS, Cláudia Dourado. |
| Contributors | SOUSA, Bianca Viana de., BARBOSA, Antonielly dos Santos., ALVES, José Jailson Nicácio ., LIMA, Lígia Maria Ribeiro. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds