Cavaco de um aço inoxidavel austenitico reciclado por metalurgia do po : uma rota alternativa para o reaproveitamento de materiais metalicos / Austenitic stainless chip recycling by powder metallurgy an alternative rote for metallic recycling

Orientador: Itamar Ferreira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-09T17:32:12Z (GMT). No. of bitstreams: 1
Delforge_DanielYvanMartin_D.pdf: 7860785 bytes, checksum: cfeec7bdb2d7e68eb7898036f0fb0ac0 (MD5)
Previous issue date: 2007 / Resumo: A reutilização dos materiais recicláveis tem como principais objetivos, minimizar os impactos ambientais e racionalizar a utilização das cadeias energéticas. No presente trabalho foram compactadas e sinterizadas amostras de mistura de cavaco de aço inoxidável austenítico AISI 316L, com pó do mesmo material. A porcentagem de cavaco variou de zero a 25% em peso, de 5 em 5%. Após a compactação, na pressão de 600MPa, as amostras foram sinterizadas, simultaneamente, na temperatura de 1473K. O comportamento mecânico do produto final foi avaliado através de Ensaios de Ruptura Transversal, recomendados e normalizados pela MPIF - Metal Powder Industries Federation e pela ASTM - American Society for Testing and Materials. As análises foram realizadas por Metalografia Convencional, associada à microscopia eletrônica de varredura nas amostras sinterizadas, resultaram em regiões de intensa difusão, portanto, regiões de sinterização de longo alcance. A resistência mecânica dos corpos-de-prova foi comparada com a resistência mecânica do aço inoxidável sinterizado, sem cavaco, determinado através do Módulo de Ruptura (MOR). A média máxima do MOR das amostras sem cavaco, foi de 457 MPa; com 5% de cavaco, de 358 MPa e com 25% de cavaco, 174MPa. Os resultados alcançados mostraram significativos valores, demonstrando ser esta uma rota alternativa para a reciclagem de cavaco de materiais metálicos, aliado à racionalização da utilização de energia e benefícios para o meio ambiente / Abstract: In the present work, samples of the mixture of 316-stainless steel chip and its powder have been sinterized. The chip weight percentage, in this particular case, has varied from zero to 25%, in increments of 5. After having been compacted under a pressure of 600MPa, all the samples were simultaneously sinterized in just one furnace batch under a temperature of 1473K. The mechanical behavior of the final product was assessed through the assays of transversal rupture test as recommended and regulated by Metal Powder Industries Federation - MPIF and by American Society for Testing and Materials ¿ ASTM. Analyses of these sinterized samples carried out by conventional quantitative metallography show areas of intense diffusion, therefore, areas of long sintered range. The mechanical strength of the assayed samples was compared to those made of sintered stainless steel, without chip. The Modulus of Rupture (MOR) achieved for samples wich contain 5%, 25% of chip and without chip were respectively 358MPa, 174MPa and 457MPa. The results achieved have overcome the expectations and there are strong evidences of the feasibility of this procedure / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264910
Date25 July 2007
CreatorsDelforge, Daniel Yvan Martin
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Ferreira, Itamar, 1952-, Ierardi, Maria Clara Fillippini, Gallego, Juno, Rodriguez, Cesar Augusto Duarte, Picon, Carlos Alberto
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format94p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds