Influência do tratamento criogênico na fadiga sob condições de fretting no Al 7050-T7451 / Influence of cryogenic treatment in fretting fatigue of Al 7050-T7451

Description

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2009. / Submitted by Jaqueline Ferreira de Souza ([e-mail]) on 2012-04-16T12:49:59Z
No. of bitstreams: 1
2009_EdgarSobralAshiuchi.pdf: 12120554 bytes, checksum: 232f69749d4ab4f8001c5983b7251fbf (MD5) / Approved for entry into archive by Leila Fernandes ([e-mail]) on 2012-04-17T11:33:42Z (GMT) No. of bitstreams: 1
2009_EdgarSobralAshiuchi.pdf: 12120554 bytes, checksum: 232f69749d4ab4f8001c5983b7251fbf (MD5) / Made available in DSpace on 2012-04-17T11:33:42Z (GMT). No. of bitstreams: 1
2009_EdgarSobralAshiuchi.pdf: 12120554 bytes, checksum: 232f69749d4ab4f8001c5983b7251fbf (MD5) / Acoplamentos mecânicos com contatos forçados estão sujeitos à falhas provocadas por variados mecanismos: deformação plástica, ruptura frágil, fadiga, corrosão, defeitos macro e microscópicos. Na prática esses mecanismos poucas vezes se apresentam isolados e não rara é a combinação de mais de dois para explicar uma falha catastrófica. Nesse trabalho investigou-se o efeito do tratamento criogênico profundo na vida por fadiga sob condições de fretting no Al 7050-T7451. Há fortes indícios da eficácia do tratamento associado ao aumento da resistência ao desgaste e aumento da vida em fadiga de alto ciclo em materiais ferrosos e isso motivou a pesquisa em fadiga sob fretting com ligas de alumínio de alta resistência de uso aeronáutico. _______________________________________________________________________________________ ABSTRACT / Mechanical couplings with forced contacts are subject to failures caused by different mechanisms: deformation, rupture fragile, fatigue, corrosion, macro and microscopic defects. These mechanisms have not always isolated and not rare is the combination of more than two to explain a catastrophic failure. This work investigate the effect of deep cryogenic treatment of fretting fatigue life of Al 7050-T7451. There is strong evidence of the effectiveness of treatment associated with increased wear resistance and increase the life in the high-cycle fatigue in ferrous materials and that motivated the search on fretting fatigue with high strength aluminum alloys of aeronautical use.

Links & Downloads

1. ASHIUCHI, Edgar Sobral. Influência do tratamento criogênico na fadiga sob condições de fretting no Al 7050-T7451. 2009. xiii, 95 f., il. Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2009.
2. http://repositorio.unb.br/handle/10482/10267

Tags

Metais - fadiga - alumínio

Contatos mecânicos

Mecânica de fratura

Additional Fields

Identifer	oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/10267
Date	23 October 2009
Creators	Ashiuchi, Edgar Sobral
Contributors	Araújo, José Alexander
Source Sets	IBICT Brazilian ETDs
Language	Portuguese
Detected Language	English
Type	info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Source	reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
Rights	info:eu-repo/semantics/openAccess