Organic photovoltaics have shown much promise as an alternative photovoltaic technology for application in low-cost, large-scale and flexible solar cells. The application of metal oxides in organic solar cells (OSCs) and the impact of the properties of metal oxide/organic hetero-interfaces on cell performance have attracted a lot of attention. The metal oxide/organic interfaces have a crucial impact on interfacial charge transfer, charge collection and the overall device performance. This thesis is aimed at clarifying the principal interfacial phenomena occurring at the metal oxide/organic hetero-interfaces as well as effective engineering of those interfacial properties in OSCs. Photo-generated electrons and holes undergo different recombination processes, e.g., bimolecular recombination and trap-assisted recombination, before being collected by the electrodes in OSCs. Light intensity-dependent current densityvoltage (JV) characteristics of OSCs were analyzed to study the effect of recombination on charge collection efficiency. Effect of metal oxide/organic hetero-interfaces on charge transfers at organic/electrode interface was analyzed using transient photocurrent (TPC) measurements. Light intensity-dependent JV characteristics and TPC characteristics were applied to explore the charge recombination dynamics in OSCs with a metal oxide interlayer. This project concentrated on an in-depth investigation of the physics and the interface phenomena such as interfacial exciton dissociation, charge recombination processes, charge collection and interface engineering for high performing OSCs. The fundamentals about light intensity-dependent J-V characteristics for OSCs were summarized. The relationship between the charge recombination dynamics and light intensity-dependent J-V characteristics in OSCs were developed. Light intensity-dependent JSC, VOC and FF in OSCs made with different bulk-heterojunction (BHJ) systems of PTB7:PC70BM, PTB7-Th:PC70BM and PNB4:PC70BM were investigated. It is found that bimolecular recombination is the most prominent factor limiting the performance of OSCs. For freshly made OSCs fabricated based on the commercial polymers, e.g. PTB7 & PTB7-Th, and the new polymer PNB4 synthesized in-house, the trap-assisted charge recombination process in the BHJ active layer plays a relatively small role. This suggests that reducing the bimolecular recombination in OSCs through selecting proper materials and device structures is crucial for enhancing the power conversion efficiency (PCE) of OCSs. In this work, device structures which enable reducing bimolecular recombination in OSCs were investigated. The effect of ZnO interlayer at the interface between BHJ and Al cathode on the performance of PTB7:PC71BM based OSCs was studied by a combination of theoretical simulation and experimental characterization techniques, e.g., using light intensity-dependent JV characteristic and TPC measurements etc. It shows that ZnO interlayer has a profound effect on the performance of the PTB7:PC70BM-based OSCs, although it does not have a significant influence on the maximum absorptance in the active layer. The origin of the improvement in the cell performance is associated with the efficient charge collection due to the favorable exciton dissociation at the electrode/active layer interface. It is shown that the presence of the ZnO interlayer allows using a thinner active layer without moderating the absorption in the optically optimized control OSCs without the ZnO interlayer. OSCs with a ~10 nm thick ZnO interlayer are found to be favorable for the efficient charge collection, and thereby improving the cell performance. The TPC measurements also reveal that the dissociation of excitons at the metal/organic interface of regular OSCs hinders the electron collection. The unfavorable interfacial exciton dissociation can be removed by interposing a ZnO interlayer at the Al/organic interface, thus bimolecular recombination at the electrode/active layer interface can be reduced for improving the charge collection efficiency. PCE of the OSCs using ZnO interlayer was 6.5%, which is about 20% higher than a control cell (5.4%), having an identical device configuration without a ZnO interlayer. Solution-processed anode interlayer, a mixture of solution-processed MoOX and PEDOT:PSS, was adopted for application in inverted PTB7:PC71BM-based OSCs. The ratio of MoOX to PEDOT:PSS in the mixed solution was optimized for achieving the best cell performance. A PCE of 7.4% was obtained for OSCs with an optimal MoOX-PEDOT:PSS based interlayer, interposed between the BHJ active layer and Ag anode, which means 10% enhancement over the PCE of control cell made with an evaporated MoOX interlayer. Light intensity-dependent JV characteristics implied that the bimolecular recombination in OSCs with a MoOX-PEDOT:PSS interlayer was reduced. TPC measurements showed that the favorable exciton dissociation occurs at the organic/MoOX interface for the inverted OSCs. The favorable interfacial exciton dissociation generates an electrical field within a very small space near the interface, contributing significant additional photocurrent when the effective bias across the active layer in the OSCs is low, and thereby assisting in an efficient charge collection at the organic/electrode interface. In addition to the improvement in the cell performance, the solution-processed MoOX-PEDOT:PSS interlayer does not require a post-annealing treatment, which is beneficial for application in solution-processed tandem and flexible OSCs.
| Identifer | oai:union.ndltd.org:hkbu.edu.hk/oai:repository.hkbu.edu.hk:etd_oa-1158 |
| Date | 04 September 2015 |
| Creators | Wu, Zhenghui |
| Publisher | HKBU Institutional Repository |
| Source Sets | Hong Kong Baptist University |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Open Access Theses and Dissertations |
| Rights | The author retains all rights to this work. The author has signed an agreement granting HKBU a non-exclusive license to archive and distribute their thesis. |
Page generated in 0.0015 seconds