This study focuses on the growth and characterization of epitaxial InAs and InAs1-xSbx. Layers are grown on InAs, GaAs and GaSb substrates by metalorganic vapour phase epitaxy, using trimethylindium, trimethylantimony and arsine as precursors. The growth parameters (V/III ratio, Sb vapour phase compositions) are varied in the temperature range from 500 ºC to 700 ºC, in order to study the influence of these parameters on the structural, optical and electrical properties of the materials. The layers were assessed by X-ray diffraction, electron and optical microscopy, photoluminescence and Hall measurements. Furthermore, the influence of hydrogenation and annealing on the electrical and optical properties of GaSb was investigated. It is shown that the growth temperature and the V/III ratio play a vital role in the resulting surface morphology of homoepitaxial and heteroepitaxial InAs layers. Growth at low temperatures is found to promote three-dimensional growth in both cases, with improvements in the surface morphologies observed for higher growth temperatures. All the investigated epilayers are n-type. It is shown that the electrical properties of heteroepitaxial InAs epilayers are complicated by a competition between bulk conduction and conduction due to a surface accumulation and an interface layer. The low temperature photoluminescence spectra of homoepitaxial InAs are dominated by two transitions. These are identified as band-to-band/excitonic and donor-acceptor recombination. The incorporation efficiency of antimony (Sb) into InAs1-xSbx is dependent on the growth temperature and the V/III ratio. Under the growth conditions used in this study, the incorporation efficiency of Sb is controlled by the thermal stability of the two constituent binaries (i.e. InAs and InSb). Changes in the low temperature photoluminescence spectra are detected with increasing x. From temperature and laser power dependent measurements, the highest energy line is attributed to band-to-band/excitonic recombination, while the peak appearing approximately 15 meV below this line is assigned to donor-acceptor recombination. The origin of an additional “moving” peak observed for higher Sb mole fraction x is tentatively attributed to quasi-donor-acceptor-recombination, arising from increased impurity/defect concentrations and a higher compensation ratio in the material. However, the unusual behaviour of this peak may also be ascribed to the presence of some degree of ordering in InAsSb. The exposure of a semiconductor to a hydrogen plasma usually leads to the passivation of shallow and deep centres, thereby removing their electrical and optical activity. In this study, the passivation and thermal stability of the native acceptor in p-type GaSb is also investigated. It is shown that this acceptor can be passivated, where after improvements in the electrical and optical properties of GaSb are observed. Upon annealing the passivated samples above 300 °C, the acceptor is reactivated.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:10548 |
| Date | January 2005 |
| Creators | Vankova, Viera |
| Publisher | Nelson Mandela Metropolitan University, Faculty of Science |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Doctoral, PhD |
| Format | 111 pages, pdf |
| Rights | Nelson Mandela Metropolitan University |
Page generated in 0.1154 seconds