Previous issue date: 2017-09-15 / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Este trabalho teve como objetivo investigar a microestrutura, resistência à corrosão e propriedades mecânicas de revestimentos produzidos por Aspersão Fria (AF) a base de: (I) pó de alumínio (Al), com ou sem alumina (Al2O3), depositados sobre aço comum; (II) revestimentos metálico-cerâmicos de WC-12Co e WC-25Co depositados sobre a liga Al7075-T6 e (III) revestimentos de cobre depositados sobre aço e obtidos a partir de pós submetidos a diferentes tratamentos. A análise dos materiais de partida e dos revestimentos, antes e após os ensaios de corrosão, foi realizada por difração a laser (DL), microscopia óptica (OM), microscopia eletrônica de varredura (SEM) acoplado a um sistema de espectroscopia de dispersão de energia de raios X (EDS) e difração de raios X (DRX). Foram realizadas medidas de dureza e ensaios de resistência ao desgaste por abrasão (Rubber Wheel) e por deslizamento (Ball on disk). A resistência à corrosão dos revestimentos foi avaliada por medidas eletroquímicas em meio de NaCl 3,5% e testes de névoa salina. Foram realizadas medidas de potencial em circuito aberto (ECA), espectroscopia de impedância eletroquímica (EIS) e curvas de polarização linear e cíclica. As imagens de SEM da secção transversal mostram que os revestimentos são densos, não possuem porosidade interconectada e nem trincas. Os resultados eletroquímicos e de névoa salina mostram que todos os revestimentos investigados protegem o substrato por longos tempos de imersão por serem compactos quando obtidos pela tecnologia de AF. Para os revestimentos a base de alumínio, os estudos mostram que o eletrólito atinge o substrato em alguns pontos somente após 2000 h de imersão e os ensaios de desgaste indicam que o revestimento compósito Al-Al2O3 apresenta melhores propriedades mecânicas. Quanto aos revestimentos metálicocerâmicos, o revestimento de WC-25Co apresentou maior espessura e também maior proteção contra corrosão até tempos maiores do que 2000 h. A caracterização dos revestimentos de cobre mostra claramente que os diferentes tratamentos dos materiais de partida exercem influência na eficiência de deposição, formação dos revestimentos e principalmente na sua resistência à corrosão. / The purpose of this work was to investigate the microstructure, corrosion resistance and mechanical properties of coatings prepared by Cold Gas Spray (CGS) based on: (I) aluminum (Al) powder with or without alumina (Al2O3), deposited on common steel; (II) WC-12Co and WC-25Co metallic-ceramic coatings deposited onto Al7075- T6 alloy and (III) copper coatings deposited onto common steel and obtained from powders submitted to different treatments. The analysis of the feedstock materials and the coatings before and after the corrosion tests were performed by laser diffraction (LD), optical microscopy (OM), scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy system (EDS) and X-ray diffraction (XRD). Hardness measurements, abrasion testing (Rubber Wheel) and sliding wear test (Ball on disk) were performed. The corrosion resistance of the coatings was evaluated by electrochemical measurements in 3.5% NaCl medium, and salt fog tests. Open circuit potential (EOC), electrochemical impedance spectroscopy (EIS), linear and cyclic polarization measurements were performed. SEM images of the cross section showed that coatings are dense, without interconnected porosity and cracks. Electrochemical and salt fog results show that all investigated coatings protect the substrate during long immersion times because they are compact when obtained by CGS technology. For the aluminum based coatings, the studies show that the electrolyte reaches the substrate at some points only after 2000 h of immersion and the wear tests show that the Al-Al2O3 composite coating has better mechanical properties. For the metal-ceramic coatings, the WC-25Co coating show higher thickness and corrosion protection up to 2000 h of immersion when compared to WC-12Co. Copper coatings characterization clearly shows that the different treatments of the feedstock materials exert influence on the deposition efficiency, coating formation and especially on their corrosion resistance. / CNPq: 153177/2014-4
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/151738 |
| Date | 15 September 2017 |
| Creators | Silva, Fernando Santos da [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Benedetti, Assis Vicente [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0027 seconds