3D printing, also known as additive manufacturing (AM), has got rapidly developed since 1987. Compared with conventional manufacturing methods, 3D printing provides some advantages such as increasing material utilization and less waste of material. Maraging steel provides good strength and toughness without losing ductility, which has been used for the 3D printing technique. Selective laser melting (SLM) is one of the 3D printing methods, which is mostly used for metal and alloy powder. In this thesis, selective laser melting will be used for maraging steel. 3D printing maraging steel is a new material, the research about the properties of 3D printing maraging steel is still ongoing. Corrosion resistance is one of the most important properties of maraging steel due to the high cost of corrosion. So this thesis will focus on the corrosion behavior of 3D printing maraging steel. The purpose of this thesis was to find the best heat treatment condition for high corrosion resistance and to find the relationship between microstructure and corrosion behavior of maraging steel. In this thesis, several kinds of maraging steel samples with different heat treatment conditions were used. SLM, SLM austenized&quenched, SLM aged, conventional austenized&quenched, and conventional aged. Besides, two kinds of solutions were produced, NaOH (pH=11.5) and Na2SO4 (pH=6.5). To observe the microstructure, an optical microscope was used. The grain size is different between SLM and conventional samples, and also different between the samples with different heat treatment conditions. The potentiodynamic polarization method was used to measuring the corrosion behavior. SLM samples have much lower current density, and the passivation potential and the corrosion rate are similar compared with conventional samples. But due to the lack of further experiments, the relationship between corrosion behavior could be affected by the combined effect of several factors.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hj-48635 |
Date | January 2020 |
Creators | Shao, Yinan |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds