Metal and oxide interactions are of broad scientific and technological interest in areas such as heterogeneous catalysis, microelectronics, composite materials, and corrosion. In the real world, such interactions are often complicated by the presence of interfacial impurities and/or high electric fields that may change the thermodynamic and kinetic behaviors of the metal/oxide interfaces. This research includes: (1) the surface hydroxylation effects on the aluminum oxide interactions with copper adlayers, and (2) effects of high electric fields on the interface of thin aluminum oxide films and Ni3Al substrate. X-ray photoelectron spectroscopy (XPS) studies and first principles calculations have been carried out to compare copper adsorption on heavily hydroxylated a- Al2O3(0001) with dehydroxylated surfaces produced by Argon ion sputtering followed by annealing in oxygen. For a heavily hydroxylated surface with OH coverage of 0.47 monolayer (ML), sputter deposition of copper at 300 K results in a maximum Cu(I) coverage of ~0.35 ML, in agreement with theoretical predictions. Maximum Cu(I) coverage at 300 K decreases with decreasing surface hydroxylation. Exposure of a partially dehydroxylated a-Al2O3(0001) surface to either air or 2 Torr water vapor results in recovery of surface hydroxylation, which in turn increases the maximum Cu(I) coverage. The ability of surface hydroxyl groups to enhance copper binding suggests a reason for contradictory experimental results reported in the literature for copper wetting of aluminum oxide. Scanning tunneling microscopy (STM) was used to study the high electric field effects on thermally grown ultrathin Al2O3 and the interface of Al2O3 and Ni3Al substrate. Under STM induced high electric fields, dielectric breakdown of thin Al2O3 occurs at 12.3 } 1.0 MV/cm. At lower electric fields, small voids that are 2-8 A deep are initiated at the oxide/metal interface and grow wider and deeper into the metal substrate, which eventually leads to either physical collapse or dielectric breakdown of the oxide film on top.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc3039 |
| Date | 12 1900 |
| Creators | Niu, Chengyu |
| Contributors | Kelber, Jeffry A., Braterman, Paul S., Chyan, Oliver M. R., Golden, Teresa D., Golden, David E., Thomas, Ruthanne D. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Copyright, Niu, Chengyu, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0019 seconds