An investigation of creep deformation in pure zirconia, using a creep-in-bending method with programmed temperature increase, showed the occurrence of superplasticity at temperatures near the monoclinic to tetragonal phase transformation. An interesting phenomenon was observed in a temporary halt to the creep process which occurred with continuing temperature increase beyond the phase transformation.
Temperature dependence tests at a maximum fibre stress of 3140 psi gave overall activation energies for the creep process in pure zirconia in the monoclinic and tetragonal phases of 44 and 103 kcal/mole respectively. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/36277 |
Date | January 1967 |
Creators | Hart, John Laurie |
Publisher | University of British Columbia |
Source Sets | University of British Columbia |
Language | English |
Detected Language | English |
Type | Text, Thesis/Dissertation |
Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.009 seconds