Previous issue date: 2018-03-26 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Neste trabalho foi avaliado o efeito da adição de polímeros estirênicos: poliestireno
(PS), copolímero estireno-acrilonitrila (SAN) e copolímero acrilonitrila-butadienoestireno
(ABS), no comportamento mecânico das blendas poliméricas formadas com o
poli(metacrilato de metila) (PMMA). As misturas foram preparadas em uma extrusora
dupla rosca e, em seguida, os corpos de prova foram moldados por injeção. Os
resultados da composição química do SAN e ABS mostraram que os percentuais de
AN encontraram-se dentro da janela de miscibilidade para as misturas com o PMMA,
isto é, de 25 e 21%, respectivamente. A análise termogravimétrica (TG) mostrou que
os polímeros estirênicos apresentaram maior estabilidade térmica do que os polímeros
acrílicos. Na reometria capilar, o PMMAe apresentou maior viscosidade dentre os
polímeros puros estudados, devido à presença das partículas casca-núcleo (CSP)
dispersas no PMMA. No índice de fluidez, a adição dos polímeros estirênicos nos dois
tipos de PMMA usados aumentaram a fluidez do material, melhorando a
processabilidade. Nas caracterizações mecânicas, observou-se que a adição de SAN
melhorou a resistência à tração e módulo de elasticidade das blendas poliméricas,
devido à presença da acrilonitrila. Nos resultados de alongamento na ruptura e
resistência ao impacto, as blendas com PMMAe apresentaram melhores resultados e,
dentre os polímeros estirênicos, o ABS teve um maior alongamento na ruptura. Na
resistência ao impacto, as blendas com SAN e ABS apresentaram resultados próximos,
mostrando indícios que a quantidade de butadieno presente nas blendas poliméricas
foram insuficiente para tenacificar o PMMA. Na dureza Shore D, observou-se que a
adição dos polímeros estirênicos nos polímeros acrílicos aumentou a dureza do
material. A análise térmica-dinâmico-mecânica (DMTA) mostrou que as temperaturas
de transição vítrea (Tg) dos polímeros se apresentaram próximas e às Tgs das blendas
poliméricas formadas foram intermediárias as dos polímeros puros. Na temperatura de
distorção térmica (HDT) e na temperatura de amolecimento Vicat observou-se que a
adição dos polímeros estirênicos aos polímeros acrílicos aumentaram a resistência
térmica dos materiais. De modo geral, a adição dos polímeros estirênicos nos dois tipos
de PMMA, mostraram resultados mecânicos melhores ou próximos aos PMMAs. / In this work the effect of the addition of styrenic polymers: polystyrene (PS), styreneacrylonitrile
copolymer (SAN) and acrylonitrile-butadiene-styrene copolymer (ABS) on
the mechanical behavior of the polymer blends formed with poly (methyl methacrylate)
(PMMA). The blends were prepared in a twin screw extruder, and then the specimens
were injection molded. The results of the chemical composition of the SAN and ABS
showed that the percentages of AN were within the miscibility window for mixtures with
the PMMA, i.e. 25 and 21%, respectively. The thermogravimetric analysis (TG) showed
that styrene polymers showed higher thermal stability than acrylic polymers. In the
capillary rheometry, the PMMAe presented higher viscosity among the pure polymers
studied, due to the presence of shell-core particles (CSP) dispersed in PMMA.
Increasing in fluidity was achieved when styrenic polymers were added to PMMA
samples, resulting in improvements in processability. In the mechanical
characterization, it was observed that the addition of SAN improved the tensile strength
and modulus of elasticity of the polymer blends due to the presence of acrylonitrile. In
the results of elongation at rupture and impact strength, blends with PMMAe presented
better results and, among styrene polymers, ABS had a greater elongation at break. In
the impact strength, blends with SAN and ABS presented close results, showing
evidence that the amount of butadiene present in the polymer blends was insufficient
to tenacify PMMA. The hardness testing (Shore D) showed improvements in hardness
when styrenic polymers were added to acrylics. Dynamic mechanical analysis (DMTA)
showed that the glass transition temperatures (Tg) of the polymers were close and the
Tgs of the polymer blends formed were intermediate those of the pure polymers. At the
heat distortion temperature (HDT) and the Vicat softening temperature it was observed
that the addition of the styrenic polymers to the acrylic polymers increased the thermal
resistance of the materials. In general, the addition of the styrene polymers in the two
types of PMMA presented mechanical results better or near the PMMAs
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/25604 |
Date | 26 March 2018 |
Creators | Pereira, Laurenice Martins |
Contributors | 40405036191, Nascimento, Maria Carolina Burgos Costa do, 03449466496, Leite, Amanda Melissa Damião, 03541569425, Brito, Gustavo de Figueiredo, 03087332402, Melo, Tomás Jeferson Alves de, 51864460415, Ito, Edson Noriyuki |
Publisher | PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.359 seconds