Orientador: Vicente Afonso Ventrella / Resumo: We carried out a study of laser welding provided "bead on plate" in micro-alloyed steel ARBL API 5L Gr. X70 in the form of plates with 1,0 x 20 x 120 mm (H x W x D). 12 welds was performed in argonic gas flow of 15 l/min, beam diameter 0,2 mm, angle of 90°, repetition rate of 9, 8, 7, 6 and 5 Hz, welding speed of 1 mm/s, gas depths focus equal to 0,57 mm below the surface of the workpiece and the pulse energy (Ep) set at 10,0 J. The time width (Lt) set at 10 ms. The heat input was varied at 90, 80, 70, 60 and 50 J/mm. The results were analyzed based on the relationship between power, weld bead geometry, corrosion, Vickers hardness, chemical analysis and microstructure. For structure revelation of the weld metals used both Nital 5%. Measures of geometry (width and depth) of the weld beads were made using images taken by digital camera on an ordinary optical microscope. Microscopy tests were carried out using a scanning electron microscope in a backscattered detector (BSD), in order to verify with greater clarity the microstructures of the samples. For verification of mechanical strength was tensile test on samples and base metal without notch insertion. For verification of hardness were analyzed four parameters being three horizontal lines and a vertical line in the center of the weld bead. To verify the corrosion, a potentiostat test was conducted for potentiodynamic polarization test where the polarization curves were analyzed. The greatest values of depth width were found i... (Resumo completo, clicar acesso eletrônico abaixo) / Mestre
| Identifer | oai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000882392 |
| Date | January 2017 |
| Creators | Sanitá, Willian Roberto Valicelli |
| Contributors | Universidade Estadual Paulista "Júlio de Mesquita Filho" Faculdade de Engenharia (Campus de Ilha Solteira). |
| Publisher | Ilha Solteira, |
| Source Sets | Universidade Estadual Paulista |
| Language | Portuguese |
| Detected Language | English |
| Type | text |
| Format | f. |
| Relation | Sistema requerido: Adobe Acrobat Reader |
Page generated in 0.0051 seconds