No / This study investigates the influence of length scale effects (micro- and macro-injection molded parts) and mold temperature on the epitaxial growth and morphological characteristics in injection-molded bars of isotactic polypropylene (iPP)/high-density polyethylene (HDPE) blends. After preparing the blends with an iPP content of 70 wt% via melt extrusion, the injection-molded bars were formed using both micro and conventional injection molding. Samples were subsequently prepared from the moulded components to allow investigation of the internal morphology using wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and polarized light microscopy (PLM). The results indicated that the matching of micro scale and appropriate mold temperature was most favorable for epitaxial crystallization. The micro-parts had a large fraction of shear layer compared with macro-parts. The SEM observations showed that the shear layer of the former consisted of a highly oriented shish-kebab structure. Moreover, the effects of different methods of injection molding on the morphological characteristics of the micro-parts and macro-parts in different layers were elucidated in detail using PLM and SEM.
| Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/10052 |
| Date | 28 January 2014 |
| Creators | Deng, D., Whiteside, Benjamin R., Wang, F., Norris, Keith, Zhang, Z. |
| Source Sets | Bradford Scholars |
| Language | English |
| Detected Language | English |
| Type | Article, No full-text in the repository |
Page generated in 0.002 seconds