Orientador : Regina Maria Puppin Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T08:28:15Z (GMT). No. of bitstreams: 1
Caldo-Teixeira_AngelaScarparo_M.pdf: 8636792 bytes, checksum: 7efc21de1fc884cb85703ee162977186 (MD5)
Previous issue date: 2003 / Resumo: Este estudo teve por objetivo avaliar a resistência da união à microtração, o padrão de fratura obtido após o ensaio mecânico e a região da união compósito/dentina, em função de tempos de condicionamento ácido (7, 15 e 20s) e sistemas de união (Single Bond-SB; Prime & Bond 2.1 - P&B2.1; One Up Bond F-OUP e Clearfil SE Bond-CSE). Foram selecionados 138 molares decíduos, hígidos, extraídos por indicações ortodônticas, de crianças na faixa etária de 4 a 9 anos. Para o ensaio de resistência da união à microtração, foram selecionados 48 dentes, aleatoriamente distribuídos em 3 grupos de acordo com o tempo de condicionamento ácido e subdivididos em 4 subgrupos de acordo com o sistema de união, sendo (n=20): G1- 7s + SB; G2- 15s + SB; G3-20s + SB; G4- 7s + P&B2.1; G5- 15s + P&B2.1; G6- 20s + P&B2.1; G7- 7s + OUP; G8- 15s + OUP; G9- 20s + OUP; G10- 7s + CSE; Gll- 15s + CSE; G12- 20s + CSE. Os dentes foram transversalmente cortados na superfície oclusal, planificados até a obtenção de área plana em dentina. Os procedimentos de união foram realizados de acordo com a distribuição dos grupos, e a superfície restaurada com compósito odontológico Filtek Z250. Em seguida, as amostras foram cortadas nos sentidos vestíbulo-lingual e mésio-distal, para obtenção de corpos-de-prova com área de secção de aproximadamente 1mm2. Após o armazenamento por 24h, os corpos-de-prova foram submetidos ao ensaio de microtração em máquina de ensaio universal (Instron) à velocidade de O ,5mm/min. Os dados foram submetidos à Análise de Variância e ao teste de Tukey). Após o ensaio mecânip,p,fodos os corpos-de-prova foram analisados quanto ao tipo de fratura em Microscópio Estereoscópico (X25) e, os compósito/dentina foram selecionados 90 dentes, distribuídos e tratados como descrito anteriormente, exceto que apenas um corte no sentido vestíbulo-lingual foi realizado, para posterior preparo para análise em MEV. As fotomicrografias foram analisadas segundo os escores: O - ausência de camada híbrida e prolongamentos resinosos; 1 - ausência de camada híbrida e presença de prolongamentos resinosos; 2 - presença de camada híbrida e ausência de prolongamentos resinosos, e 3 - presença de camada híbrida e prolongamentos resinosos. Os dados obtidos foram submetidos à análise estatística (Teste de Kruskal-Wallis). De acordo com os resultados pôde-se concluir que: 1 - A diminuição no tempo de condicionamento ácido (7s) não interferiu nos valores de resistência da união compósito/dentina, para todos os sistemas de união utilizados neste estudo; 2 - Houve correlação negativa, apenas, entre a interação P&B2.1*tempo de condicionamento; 3 - A análise do padrão de fratura demonstrou maior predominância de falhas mistas para todos os grupos, exceto P&B 2.1, cujas falhas encontradas para os tempos de 7 e 15s foram adesivas e para o tempo de 20s coesiva em compósito; 4 - Quanto ao aspecto morfológico da união compósito/dentina pôde-se observar que a formação de camada híbrida e prolongamentos resinosos mostrou relação direta com o sistema de união utilizado / Abstract: The aim of this study was to evaluate the micro-tensile bond strength, the failure sites obtained after the test, and the resin/dentin interface, in different etching times (7, 15, and 20s) and with different bond systems (Single Bond-SB; Prime & Bond 2.1- P&B2.1; One Up Bond F-OUP e Clearfil SE Bond-CSE). 138 sound extracted primary teeth were selected. For the micro-tensile bond strength, 48 teeth were selected and randomly distributed into 3 groups, according to etching time, and subdivided into 4 subgroups, according to bond systems as follows (n=20): G1- 7s + SB; G2- 15s + SB; G3- 20s + SB; G4- 7s + P&B2.1; G5- 15s + P&B2.1; G6- 20s + P&B2.1; G7- 7s + OUP; G8- 15s + OUP; G9- 20s + OUP; G1Q- 7s + CSE; Gll- 15s + CSE; G12- 20s + CSE. The teeth were obliquely cut on the occlusal surface and flatenned until dentin area was reached. The bonding procedures were carried out according to groups, and the restorative procedure was carried out using the resin composite Filtek Z250. Next, the samples were sectioned in buccal-lingual and mesio-distal orientations, to obtain samples of about lmm2. The samples were stored in distilled water at 3-rC for 24h, and then submitted to micro-tensile bond strength in a Universal Testing Machine (Instron) with a crosshead speed of 0.5mm/min. The data were submitted to ANOV A and Tukey's test (p<0.05). The failure sites obtained after the test were observed, for failure type, in stereoscope microscopy of 25X magnification, and the representative failures of each group were observed in Scanning Electron Microscopy (SEM). 90 teeth were selected for the analysis of resin composite/dentin. The teeth were distributed and treated as previously described, except that just one. The photomicrographs were analyzed according to scores: o - absence of hybrid layer and resin tags; 1- absence of hybrid layer and presence of resin tags; 2 - presence of hybrid layer present and absence of resin tags, and 3 -presence of hybrid layer and resin tags. The data obtained were submitted to Kruskal-Wallis's testo According to the results it could be concluded that: 1 -the decrease in etching time (7s) did not interfere in bond values, for ali bond systems used; 2- there was negative correlation, solely, between P&B2.1*etching time interaction; 3 - the pattern of failure analysis showed major predominance of mixed failures for ali groups tested, except P&B 2.1, where failures for 7 and 15s were adhesives and for the 20s were composite cohesive; 4 - the resin composite/dentin area showed that the formation of hybrid layer and resin tags showed direct relation with the bond system used. / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288593 |
| Date | 05 May 2003 |
| Creators | Caldo-Teixeira, Angela Scarparo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Rodrigues, Celia Regina Martins Delgado, Goes, Mario Fernando de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 206p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds