Orientador: Lourenço Correr Sobrinho, Evandro Piva / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T10:27:36Z (GMT). No. of bitstreams: 1
Dias_MyrnaCarvalho_D.pdf: 1118251 bytes, checksum: 3d98e2abfaec81424cc59b34ec8d154e (MD5)
Previous issue date: 2007 / Resumo:O objetivo deste estudo foi avaliar a influência da microestrutura e espessura das cerâmicas prensadas na intensidade e transmitância da luz e na eficiência da polimerização do cimento resinoso de dupla ativação Variolink II, fotoativado através de duas cerâmicas prensadas reforçadas com cristais de leucita. Foram confeccionados amostras das cerâmicas IPS Empress (EMP) e IPS Empress Esthetic (EST) com 0,7; 1,4 e 2,0mm e IPS Empress 2 (E2) com 0,8 e 1,1mm de espessura. E2 com 0,8mm foram cobertos com IPS Eris E2 dentina (D) para a obtenção de discos com 1,2 e 1,4mm. E2+D foram cobertos com IPS Eris esmalte (E) para alcançar a espessura final de 1,5mm. O mesmo procedimento foi realizado em E2 com 1,1mm (E2+D= 1,6 e 1,9mm e E2+D+E=2,0mm). A intensidade de luz gerada pelos aparelhos de fotoativação de lâmpada halógena convencional (XL 2500/3M ESPE) e LED (Ultrablue Is/DMC) foi verificada com radiômetro (Hilux), com e sem a presença da cerâmica sobre o sensor de leitura. O percentual de transmitância de luz através das cerâmicas foi obtido com auxílio do espectofotômetro Lambda 9. O grau de polimerização do Variolink II foi realizado em corpos-de-prova com 1,0mm de altura, fotoativados diretamente e indiretamente (sob EMP e EST com 0,7; 1,4 e 2,0mm), por 40 s utilizando o aparelho de lâmpada halógena convencional. A dureza Knoop foi analisada imediatamente e após 24 horas de armazenagem. A análise da microestrutura das cerâmicas EMP e EST foi verificada pelo MEV e por difração de raio-X. Os resultados mostraram que os valores de intensidade de luz emitidos pelas unidades de fotoativação sobre o EST foram estatisticamente superiores em relação ao EMP (p<0,05) e os valores obtidos pelo E2 foram maiores do que quando cobertos com D (p<0,05). Os valores de intensidade de luz diminuíram com o aumento da espessura das cerâmicas prensadas. A lâmpada halógena convencional gerou valores de densidade maiores do que o LED. Os gráficos espectrais obtidos pela transmitância da luz por meio das cerâmicas prensadas confirmaram os resultados alcançados pela intensidade de luz. O valor de dureza do cimento polimerizado sob o EST foi maior do que sob EMP (p<0,05), o grau de polimerização do cimento foi maior após 24 horas de armazenagem (p<0,05) e os discos com 2,0mm de espessura promoveram dureza menor do cimento após 24 horas (p<0,05). O MEV mostrou que os cristais de leucita no EST apresentaram-se mais densamente distribuídos na matriz vítrea do que no EMP. A difração de raio-X confirmou a mesma cristalinidade do EMP e EST. Concluiu-se que as alterações na microestrutura e espessura das cerâmicas prensadas influenciaram na intensidade e transmitância de luz e o EST promoveu melhor grau de polimerização do cimento resinoso Variolink II que o EMP / Abstract: The aim of this study was to evaluate the influence of the microstruture and thickness of the pressable ceramic in the intensity and light transmittance and the polymerization efficiency of the dual resin-based cement Variolink II cured beneath two hot-pressed ceramic reinforced with leucite crystals. IPS Empress (EMP) and IPS Empress Esthetic (EST) with 0.7; 1.4 and 2.0mm and IPS Empress 2 (E2) with 0.8 and 1.1mm of thickness were made. E2 with 0.8mm were covered with IPS Eris E2 dentin (D) for obtaining disks with 1.2 and 1.4mm. E2+D were covered with IPS Eris E2 enamel (E) to reach the final thickness of 1.5mm. The same procedure was realized in E2 with 1.1mm (E2+D = 1.6 and 1.9mm and E2+D+E=2.0mm). The light intensity emitted by the light curing units quartztungsten-halogen (XL 2500/3M ESPE) and LED (Ultrablue Is/DMC) was assessed by the digital radiometer Hilux with na without the presence of the disks of ceramic on sensor. The percentage of light transmittance for the pressable ceramic was obtained by the spectrophotometer Lambda 9. The degree of polymerization of Variolink II was realized from resin cements specimens with 1.0mm of height, cured directly and indirectly (under EMP and EST with 0.7; 1.4 and 2.0mm), for 40s using the light curing units quartz-tungsten-halogen. The hardness Knoop was analyzed the immediately and 24 hours after photoactivation. The analysis of the microstructure of the pressable ceramic was realized by EDX and SEM and for the X-ray diffraction of EMP and EST. The results showed that the values of light intensity emitted for light curing units on EST were higher than of EMP (p <0.05) and the values obtained by E2 were larger than when covered with D (p <0.05). The values of light intensity decreased with the increase of the thickness of the pressable ceramic. The quartz-tungsten-halogen emitted light intensity higher than LED. The graphs obtained by the light transmittance through the pressable ceramic confirmed the results reached by the light intensity. The value of hardness of the cement cured under EST was higher than under EMP (p <0.05), the degree of polimerization of the cement was higher after 24 hours of storage (p <0.05) and disks with 2.0mm of thickness obtained a smaller hardness of the cement after 24 hours (p <0.05). MEV showed that the leucite crystals in EST presented more homogeneous distributed in the glassy matrix than in EMP. EDX revealed the presence of titanium oxide in composition of D. The ray-X diffraction confirmed the same cristallinity of EMP and EST. It was concluded that changes in the microstructure and thickness of the pressable ceramic influenced in the light intensity and transmittance and EST showed a better degree of polimerization of the dual resin-based cement than EMP / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289600 |
| Date | 10 November 2007 |
| Creators | Dias, Myrna Carvalho |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Piva, Evandro, Correr Sobrinho, Lourenço, 1960-, Tiburcio, Manio de Carvalho, Lopes, Murilo Baena, Consani, Simonides, Consani, Rafael Leonardo Xediek |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 51p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds