In the Visual - Weld and Sysweld programs, a simplified simulation of the welding process of the turbine rotor made of 27NiCrMoV 15-6 substance was performed. The numerical analysis took place at the equal temperature of preheating and it covered both minimal and maximal percent chemical composition. The simulation proved that the percent deviations of elements in the substance change the speed necessary for reaching of the bainitic structure. Simulation results were verified by a practical experiment. Two weld beads were welded to a base substance by MIG method: one bead at the temperature of 200°C, the other one at the temperature of 300°C, both with the same specific input caloric QS. Both micro and macrostructure of the base substance and TOO was evaluated, and the progression of the hardness was measured as well. The deviations fell within the acceptable 15% range.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:231034 |
Date | January 2013 |
Creators | Cvoligová, Hana |
Contributors | Kubíček, Jaroslav, Daněk, Ladislav |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds