AA5083-H321 is an aluminum alloy commonly used in ship hull superstructures as it has a corrosion resistance which affords an excellent degree of protection in chloride-rich marine environments. Corrosion performance can degrade in a process called sensitisation, due to the precipitation of a β-phase onto grain boundaries with exposure to elevated temperatures over decades of service. Friction Stir Processing (FSP) has been evaluated as a method for locally reversing the degraded microstructure and removing a susceptibility to Intergranular Corrosion (IGC) in immersed and atmospheric conditions. Both the mechanical stirring and heat input to the plate by an FSP tool have been shown to remove the β-phase from grain boundaries which had been precipitated by a sensitisation heat treatment. Sensitisation was shown to cause intergranular corrosion of the alloy; however this susceptibility was removed after microstructural modification by FSP. A re-sensitisation treatment of the previously sensitised and FSP’d region was seen to precipitate coarser and more discrete β-phase particles onto grain boundaries, which corroded at a faster rate than the once-sensitised material under electrochemical testing. This indicates that corrosion resistance degrades more quickly with subsequent sensitisation.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:600331 |
| Date | January 2014 |
| Creators | Meredith, Gavin Simon |
| Publisher | University of Birmingham |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://etheses.bham.ac.uk//id/eprint/4932/ |
Page generated in 0.0017 seconds