Previous issue date: 2015-02-11 / CNPq / Este estudo visa avaliar a influência de um oligômero multifuncional de estirenoacrílico (POLYAD PR 002), comercializado como extensor de cadeia para polímeros de condensação, no aumento da massa molar do poli (tereftalato de etileno) (PET) e, consequentemente, na restituição de suas propriedades reológicas. O comportamento foi analisado em PET pós-consumo (PETPC) oriundo de garrafas incolores do estado da Paraíba, bem como no PET virgem (PETV) para um parâmetro comparativo. Os polímeros foram processados sem e com a incorporação do aditivo extensor de cadeia em diferentes níveis, para possibilitar o desenvolvimento de diferentes grades de PET. Foi utilizado um misturador interno acoplado ao reômetro de torque Haake Rheomix 3000QC da PolyLab QC, com rotores do tipo roller operando a 265ºC e 60 rpm. Na primeira etapa, o processamento foi realizado em um tempo de 16 min, empregando diferentes concentrações do aditivo (1,5%, 3% e 5% em massa), e na segunda etapa os polímeros sem e com a incorporação do aditivo extensor, nas concentrações 1,5 e 3% em massa, foram processados e reprocessados em um tempo de 30 min. As amostras obtidas foram caracterizadas por reometria de torque. A partir de medições de torque e temperatura obtidas pelo equipamento foi possível realizar uma avaliação das massas molares. De acordo com os resultados, confirma-se que as estimativas com base em medições de torque em tempo real são indicadores rápidos e precisos da eficácia da extensão da cadeia no PET e que a incorporação do aditivo ao PETV e ao PETPC teve uma forte influência no aumento da sua massa molar. / This study is concerned with the effect of a styrene-acrylic multifunctional oligomer (POLYAD PR 002), marketed as a chain extender for condensation polymers, in the increase of molecular weight of poly (ethylene terephthalate) (PET) and, consequently, the restitution of their rheological properties. This behavior was analyzed in post-consumer PET (PETPC) from colorless bottles collected in the State of Paraíba, as well as in virgin PET (PETV) for comparison. The polymers were processed with and without the incorporation of the chain extender additive at different levels to facilitate developing different grades of PET. An internal mixer coupled to the torque rheometer Haake Rheomix 3000QC of PolyLab QC, with roller type rotors operating at 265ºC and 60 rpm was used. In the first stage, processing was performed during 16 min, with different additive concentrations (1.5%, 3% and 5% by weight) and in a second stage, polymers with and without the incorporation of additive concentrations 1.5 and 3% by weight were processed and reprocessed during 30 min. The samples were characterized by torque rheometry. From torque and temperature measurements was possible to evaluate molar masses. According to the results, it is evident that estimates based on realtime torque measurement are fast and accurate indicators of the effectiveness of chain extension, and that the incorporation of the additive to PETV and PETPC had a strong effect in increase its molar mass
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1159 |
| Date | 12 July 2018 |
| Creators | TAVARES, Albaniza Alves. |
| Contributors | SILVA, Suédina Maria de Lima., CANEDO, Eduardo Luís., TEÓFILO, Edvânia Trajano., ANDRADE, Daniela de Lourdes Anjos Coutinho Simões. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds