The Mo-Ni-Re system is one of the important subsystems of the Ni based superalloys engineered for use in high temperature applications. Considering the contradictions among previously reported information, the present study was devoted to the complete experimental determination of the phase equilibria in the Mo-Ni-Re system, structural characterization of its intermetallic phases and thermodynamic modeling of the system with the help of the CALPHAD method. The experimental investigation of phase equilibria was carried out with the help of equilibrated alloys and phase diagrams of the Ni-Re and Mo-Ni-Re system (at 1200°C and 1600°C) were proposed. In comparison with previous investigations, the Ni-Re phase diagram determined during the present study showed significant difference in terms of homogeneity domains, freezing ranges and peritectic reaction temperature. The 1200°C isothermal section of the Mo-Ni-Re system proposed during the present study showed large extension of the Mo-Re σ phase and Mo-Ni δ phase in the ternary region. In addition, presence of two previously unknown ternary phases was also observed. The isothermal section of the Mo-Ni-Re system at 1600°C also showed large extension of σ phase in the ternary region whereas extension of the Mo-Re χ phase in both isothermal sections was restricted to narrow composition range. The presence of the ternary phases observed in the 1200°C isothermal was not evidenced in 1600°C isothermal section. On the other hand, partial investigations of phase boundaries in the Mo-Ni and Mo-Re binary systems and determination of liquidus projection of the Mo-Ni-Re system was also carried out. The liquidus projection of the Mo-Ni-Re system proposed during present study also showed largely extended primary crystallization fields of the Mo-Re σ phase and Re solid solution in the ternary region. Since isothermal sections of the Mo-Ni-Re system showed largely extended homogeneity domain of σ, structural characterization of the Mo-Ni-Re σ with particular emphasis on determination of site occupancy trends as a function of composition was carried out by combined Rietveld refinement of the X-ray and neutron diffraction data. The experimental results gathered during the present study along with the information available in the literature were used as input for thermodynamic modeling of the Mo-Ni-Re system. The thermodynamic description of the Mo-Re system was taken from literature whereas thermodynamic modeling of the Mo-Ni, Ni-Re and Mo-Ni-Re system was carried out during the present study with the help of the CALHAD method.Keywords: Mo-Ni; Mo-Re; Ni-Re; Mo-Ni-Re; phase diagram; isothermal section; structural characterization; thermodynamic modeling; CALPHAD method
| Identifer | oai:union.ndltd.org:CCSD/oai:tel.archives-ouvertes.fr:tel-00805384 |
| Date | 20 December 2012 |
| Creators | Yaqoob, Khurram |
| Publisher | Université Paris-Est |
| Source Sets | CCSD theses-EN-ligne, France |
| Language | English |
| Detected Language | English |
| Type | PhD thesis |
Page generated in 0.0025 seconds