Standard methods for fire resistance testing require large-scale assemblies and are typically conducted on specialized furnaces at considerable cost. This research focused on developing a scaling methodology for a reduced-scale fire resistance test that reduces the size of the test article while maintaining the same thermal and structural response exhibited in the large-scale test. The developed scaling methodology incorporates uniform geometric scaling, Fourier number time scaling, and furnace boundary condition matching. The scaling laws were experimentally validated with fire exposure tests on gypsum wallboard samples at three scales (full-scale, 1/2-scale, and 1/6-scale). Next, these scaling laws were demonstrated for wood with combined thermo-structural loading. Dimensional lumber boards at ½-scale and ¼-scale were subjected to combined bending and thermal loading. Samples were placed in static three-point bending with the loading scaled to have structural similitude, while simultaneously, the bottom surface was exposed to a scaled fire exposure. Analytical modeling of wood pyrolysis demonstrated that, due to char kinetics as the heating rate is increased in the tests, equivalently less char is formed in the reduced-scale tests. Therefore, we developed a char timescale correction factor, calculated from both model predictions and measured charring rates, which modified the previous Fourier number time scaling laws. Finally, we investigated the effect of multi-orientation materials with a similar set of combined thermo-structural three-point bending tests on plywood samples. The stacking sequence of laminated wood significantly impacts the composite mechanical behavior of the material, especially when scaling down thermo-mechanical tests on plywood. A consequence of the different stacking sequences is that the data from the reduced-scale test cannot be directly scaled to predict the behavior of the larger-scale tests. Thus, modeling becomes essential to extrapolating the data from the reduced-scale test to predict the behavior of the larger-scale test. Reduced cross-sectional area models incorporating classical lamination theory were used to predict the mechanical response of the composite samples as the char front increased. / Doctor of Philosophy / How do we know that a structure will be safe during a fire? The response of structures to fire is typically evaluated using large-scale tests with combined thermo-structural loading: one side of the test sample is exposed to a furnace at standard gas temperatures, while at the same time the sample is loaded with a structural load. Fire resistance testing is essential to evaluating if building components can maintain structural integrity and allow people to egress a building safely during a fire. Standard methods for fire resistance testing require large-scale test samples and are typically conducted on specialized furnaces at national testing facilities at considerable cost. In order to support research and development efforts to design new fire-resistant structures, reduced-scale tests are more desirable because they are cost-effective. However, no reduced-scale test exists to evaluate fire resistance. This research focused on developing a methodology for reducing the size of a test with combined thermo-structural loading. The goal is to have a reduced-scale test that provides insight into the thermal and structural behavior of a similar sample in the large-scale test. The test scaling laws were demonstrated with both experiments and modeling. We developed a small-scale furnace setup to conduct combined thermo-structural tests on samples of different scales. To investigate material type, we tested samples made from gypsum wallboard, dimensional lumber, and plywood. This work will ultimately allow manufacturers to replace costly standard fire resistance tests with reduced-scale versions of these tests during the material screening phase.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/114193 |
| Date | 27 March 2023 |
| Creators | Gangi, Michael Joseph |
| Contributors | Engineering Science and Mechanics, Case, Scott W., Lattimer, Brian Y., Dillard, David A., Frazier, Charles E., Kapania, Rakesh K. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | English |
| Detected Language | English |
| Type | Dissertation |
| Format | ETD, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0023 seconds