The subject of the doctoral thesis is the study of moisture resistance of macro-defect-free (MDF) composites based on calcium-aluminate cement and polyvinylalcohol used as polymer. MDF cements are perspective materials providing unique properties relative to traditional cement pastes with great potential to incoming constructional utilization. But it is known that MDF cements exhibit sensitivity to water, with swelling and reduction of strength. Therefore the work is aimed in monitoring of an organic polymer effect on the moisture resistance of MDF materials and phase changes. The effects of three different organotitanate cross-linking agents on the properties were investigated. The organotitanate-modified MDF cement samples exhibited improved moisture resistance as compared to the standard samples when exposed to 100 % relative humidity or water at laboratory conditions. The influence of composition at different curing on the properties of model MDF cement samples was observed. The characterization of MDF samples was based especially on test of flexural strength, XRD, DTA/TGA and EGA, EDS and scanning electron microscopy analyses.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:233354 |
| Date | January 2012 |
| Creators | Másilko, Jiří |
| Contributors | Palou, Martin, Drábik, Milan, Havlica, Jaromír |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds