This thesis reports quasi steady state photoinduced absorption measurements from three conjugated polymers: polypyridine (PPy), polyfluorene (PFO) and the emeraldine base (EB) form of polyaniline. The aim of these experiments was to determine the nature of the photoexcited states existing in these materials in the millisecond time domain, as this has important consequences for the operation of real devices manufactured using these materials. The results from the photoinduced absorption experiments are closely compared with published results from pulse radiolysis experiments. In all cases there is very good correspondence between the two data sets, which has enabled the photoexcited states to be assigned with a high degree of confidence. Quasi steady-state photoinduced absorption involves the measurement of the change in absorption of a material in response to optical excitation with a laser beam. The changes in absorption are small, so a dedicated instrument was developed and optimised for each different sample. Lock-in techniques were used to recover the small signals from the samples. The samples involved were thin films of the polymer spin coated onto sapphire substrates in the cases of PPy and EB. Solution state experiments were conducted on EB. The experiments on PFO were conducted on aligned and unaligned thin films provided by Sony. In the case of the aligned PFO samples, the photoinduced absorption spectrometer was modified to enable polarisation-sensitive data collection. In PPy, both triplet excitons and polarons have been shown to be long-lived photoexcitations, with photoinduced absorption features at 2.29 eV (triplet excitontransition), 1.5 eV and 0.8 eV (polaron transitions). In PFO, the one observed photoinduced band at 1.52 eV is assigned to a triplet exciton. Two photoinduced absorption bands are observed in EB, at 1.4 eV and 0.8 eV. These are assigned to aself-trapped CT singlet exciton and triplet exciton, respectively.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:269911 |
| Date | January 2002 |
| Creators | Hartwell, Lewis John |
| Publisher | Durham University |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://etheses.dur.ac.uk/2020/ |
Page generated in 0.0015 seconds