Propuesta de diseño de las propiedades mecánicas del concreto con adición de viruta de acero fundido en reemplazo parcial del agregado fino / Design proposal of the mechanical properties of concrete with the addition of molten steel shavings in partial replacement of fine aggregate

En la presente investigación realizada se evaluaron las propiedades físicas de los agregados, para el cual se ejecutó diseños de mezclas con la finalidad de determinar las propiedades mecánicas del concreto adicionado con viruta de acero fundido en porcentajes de 3% ,6% y 9% como reemplazo parcial del agregado fino.

La finalidad de evaluar las propiedades mecánicas del concreto adicionado con viruta de acero fundido, es comprobar la resistencia a la compresión, tracción y flexión en los diferentes porcentajes y edades.

Para los ensayos se realizaron diseños de concreto patrón y concreto con adición de viruta acero fundido, según la norma (ACI 211, 2009) para una resistencia a la comprensión de 210 kg/cm2.

El estudio estimo la evaluación de las propiedades mecánicas del diseño de concreto patrón en estado fresco (temperatura, slump, peso unitario), y en estado endurecido (resistencia a la compresión, flexión y tracción), evaluación que se realizó también en el diseño de concreto con adición de viruta de acero fundido al 3%, 6% y 9%.

Al finalizar los ensayos se observó que el diseño de estudio de concreto con adición de viruta de acero fundido aumenta su resistencia a la compresión, flexión y tracción. / In the present investigation carried out, the physical properties of the aggregates were evaluated, for which mixture designs were executed in order to determine the mechanical properties of the concrete added with molten steel shavings in percentages of 3%, 6% and 9% as partial replacement of fine aggregate. The purpose of evaluating the mechanical properties of concrete added with molten steel shavings is to check the resistance to compression, traction and bending in the different percentages and ages. For the tests, designs of standard concrete and concrete with addition of cast steel shavings were made, according to the (ACI 211, 2009) standard for a resistance to compression of 210 kg / cm2. The study estimated the evaluation of the mechanical properties of the pattern concrete design in the fresh state (temperature, slump, unit weight), and in the hardened state (resistance to compression, bending and traction), evaluation that was also carried out in the design of concrete with addition of 3%, 6% and 9% cast steel shavings. At the end of the tests, it was observed that the concrete study design with the addition of molten steel shavings increases its resistance to compression, bending and traction. / Tesis

Identiferoai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/655018
Date05 February 2021
CreatorsRiveros Maita, Gilmar, Vilca Canchapoma, John Juady
ContributorsHuerta Campos, Carlos Alberto
PublisherUniversidad Peruana de Ciencias Aplicadas (UPC), PE
Source SetsUniversidad Peruana de Ciencias Aplicadas (UPC)
LanguageSpanish
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/bachelorThesis
Formatapplication/pdf, application/epub, application/msword
SourceUniversidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico - UPC
Rightsinfo:eu-repo/semantics/openAccess, Attribution-NonCommercial-ShareAlike 4.0 International, http://creativecommons.org/licenses/by-nc-sa/4.0/

Page generated in 0.0018 seconds