Orientadores: Luis Alexandre Maffei Sartini Paulillo, Mario Fernandes de Goes, Van P. Thompson / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T23:14:53Z (GMT). No. of bitstreams: 1
Souza_GraceMendoncaDiasde_D.pdf: 4922491 bytes, checksum: 26ef96d5e0d142ac1640c476b8484024 (MD5)
Previous issue date: 2006 / Resumo: A dificuldade em se obter valores de união elevados e duradouros entre cimento resinoso e cerâmicas de alto conteúdo cristalino tem limitado o emprego destes materiais. Desta maneira, o objetivo deste estudo foi avaliar a resistência de união entre dois cimentos resinosos e uma cerâmica à base de dióxido de zircônio após diferentes tratamentos superficiais da cerâmica. Trinta e seis amostras semi-circulares em cerâmica e compósito foram polidas até a granulação 600µm. Antes da cimentação as amostras de cerâmica (n=3) foram tratadas com duas soluções básicas: hidróxido de sódio (Na) ou hidróxido de tetrabutilamônio (Ta); e um primer para metal (Ap), e o primer foi associado ou não às soluções. Amostras sem tratamento foram utilizadas como controle. A cimentação foi realizada empregando-se dois cimentos contendo monômeros fosfato ¿ RelyX Unicem (RU) e Panavia 21 (Pa) ¿ sob aplicação de carga de 600g. Depois de 24 horas, as amostras foram seccionadas em dois eixos a fim de se obter 40 palitos por amostra aproximadamente, com uma interface adesiva de cerca de 0,8mm2, que foram armazenados em água destilada, a 37ºC, e testadas em dois tempos: após 72 horas (TI) ou após 60 dias+termociclagem (5-55oC/5000 ciclos) (TF). O teste de resistência de união foi realizado à velocidade de 1mm/min em máquina universal de ensaios. Os valores em Megapascal foram submetidos à Análise de Variância (ANOVA) e ao Teste de Variação Múltipla de Tukey (p>0,05). Os resultados apresentados foram: TI ¿ ApRU-28,53a, NaApRU-23,31ab, NaApPa-22,15ab, TaApPa-19,98b, TaPa-19,98b, NaPa-19,96b, ApPa-19,92b, TaRU-18,16b, TaApRU-17,53b, Pa-17,16bc, RU-10,79c, NaRU-10,49c; TF ¿ ApRU-31,69A, NaApPa-19,17B, NaApRU-17,91BC, TaApPa-16,00BCD, TaPa-7,76CDE, ApPa-6,94CDE, NaPa-5,61DE, TaApRU-3,94E, TaRU-3,61E, RU-2,85E, Pa-1,88E, NaRU-0,27E. Através dos resultados obtidos, foi possível concluir que o maior valor de resistência de união no tempo inicial foi apresentado pela associação primer para metal e RelyX Unicem, mantendo médias com valores semelhantes após o envelhecimento. Para o cimento Panavia, não houve diferença estatística entre todos os tipos de tratamento no tempo inicial. Após o envelhecimento, a associação de primer para metal e solução básica resultou nos maiores valores de resistência de união para o cimento Panavia / Abstract: The difficulty to obtain high and durable bond strength values between high crystalline content ceramics and resin luting system has reduced the employment of those materials. The purpose of this study was to evaluate the bond strength between two luting systems and zirconium dioxide ceramic after different ceramic¿s surface treatment. Thirty-six half-circled shaped composite and zirconia samples were roughened up to 600 grit carbide silicon paper. Before the luting steps, samples (n=3) were treated either with basic solutions: sodium hydroxide (Na) or tetrabutylammonium hydroxide (Ta); or with a metal primer (Ap) and the primer was also combined with the basic solutions. Samples with no treatment were considered as control. The cementation was done employing two phosphate monomer containing systems - RelyX Unicem (RU) and Panavia 21 (Pa) ¿ under 600g loading. After 24 hours, samples were cut in two axis in order to obtain 40 beams per sample approximately, with an adhesive interface about 0.8mm2, and were placed in deionized water at 37ºC, being tested in two different times: 72 hours (TI) or after 60 days+thermocycling (5-55oC/5000 cycles) (TF). Bond strength test was conducted at 1mm/min crosshead speed in an universal testing machine. The values in MPa were analyzed through Analysis of Variance (ANOVA) and LSMeans Test (p>0.05). The results presented were: TI ¿ ApRU-28.53a, NaApRU-23.31ab, NaApPa-22.15ab, TaApPa-19.98b, TaPa-19.98b, NaPa-19.96b, ApPa-19.92b, TaRU-18.16b, TaApRU-17.53b, Pa-17.16bc, RU-10.79c, NaRU-10.49c; TF ¿ ApRU-31.69A, NaApPa-19.17B, NaApRU-17.91BC, TaApPa-16.00BCD, TaPa-7.76CDE, ApPa-6.94CDE, NaPa-5.61DE, TaApRU-3.94E, TaRU-3.61E, RU-2.85E, Pa-1.88E, NaRU-0.27E. Based on the results obtained, it was possible to conclude that the combination primer and RelyX Unicem presented the highest values, which were maintained after aging. For Panavia system, there was not significant statistical difference among all the treatments employed at the initial time. After aging, the association metal primer and basic solution produced the highest bond strength values for Panavia system / Doutorado / Dentística / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289656 |
| Date | 27 January 2006 |
| Creators | Souza, Grace Mendonça Dias de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Goes, Mario Fernando de, 1954-, Thompson, Van P, Paulillo, Luis Alexandre Maffei Sartini, 1962-, Thompson, Van P., Martins, Luís Roberto Marcondes, Braga, Roberto Ruggiero, Giannini, Marcelo |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 103p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0063 seconds