Previous issue date: 2008-12-19 / O Brasil está, atualmente, entre os maiores produtores de grãos do mundo, em especial o arroz. Com o beneficiamento deste produto são geradas grandes quantidades de resíduos (casca) que ocasionam problemas ambientais, pela deposição inadequada no meio ambiente e por seu longo tempo de degradação. A incorporação destes resíduos industriais a componentes para construção civil, como concretos e argamassas, é uma das possíveis soluções para o aproveitamento de subprodutos poluentes estando em acordo com os princípios da sustentabilidade. Este trabalho tem como objetivo estudar a durabilidade de argamassas convencionais e alternativas incorporadas com resíduos de cinza da casca de arroz substituindo parte do aglomerante e casca de arroz substituindo o agregado miúdo, através do envelhecimento acelerado, por ciclos de molhagem e
secagem. Inicialmente foi realizada com as matérias-primas convencionais e alternativas uma caracterização física, química e mineralógica através dos seguintes ensaios: análise granulométrica por peneiramento e difratometria a laser, área especifica, massa unitária, análise química, difração de raios X, análise térmica diferencial e gravimétrica. Para avaliar a durabilidade pelo método do envelhecimento acelerado, por ciclos de molhagem e secagem, foram confeccionados corpos-deprova de argamassas convencionais e argamassas alternativas nos traços 1:4; 1:6 e 1:8 incorporando 3%, 6%, 9%, 15%, 20% e 30% de resíduo de cinza de casca de arroz em substituição ao aglomerante e 10%, 20% e 30% de casca de arroz em substituição ao agregado miúdo por períodos de cura de 28, 63, 91, 180 e 360 dias. As propriedades físico-mecânicas determinadas foram: absorção de água, densidade aparente e resistência. Os resultados dos ensaios de caracterização das matérias-primas convencionais (cimento e agregado miúdo) e alternativos (cinza e casca de arroz) encontram-se dentro dos padrões estabelecidos pelas normas da ABNT,
indicando superfície específica e índice de finura da cinza de casca de arroz bem superior a do cimento empregado. Os resultados evidenciaram que a cinza de casca de arroz é predominantemente amorfa e tem alta pozolanicidade de acordo com as especificações da ABNT, possibilitando seu uso em concretos e argamassas pelas suas características de grande finura. Em relação ao comportamento mecânico, foram encontrados valores superiores dos corpos-de-prova alternativos incorporados com cinza de casca de arroz em relação aos convencionais mesmo quando expostos ao envelhecimento acelerado, enquanto os corpos-de-prova das argamassas incorporados com casca de arroz apresentaram valores dentro das especificações da ABNT e inferiores aos convencionais, comprovando a viabilidade técnica da utilização destes resíduos,uma vez que não se evidenciou influência na durabilidade, além de ser uma medida ecologicamente correta. / Brazil is one of the greatest producers of grain in the world, especially in rice. With the industrialization of this product great amount of waste (husk) is generate and cause environmental problems, by the inadequate discharge in the environment and by the long time to deteriorate. The incorporation of this industrial residue as components to civil construction, as concrete and mortars, is one of the possible solutions to use this pollutants sub products and this is in agreement with the sustainable principle. The aim of this work is to study the durability of the conventional and alternative mortars incorporated with husk rice ash residue by substituting part of the agglomerate and rice husk substituting small aggregate. The durability was study by the accelerate weathering (by wetting and drying cycles). Firstly it was done a physical, chemical and mineralogical characterization of the conventional and alternatives raw materials by the following techniques: particle size by sieving and laser diffraction, surface area, specific mass,
chemical analysis, X-rays diffraction, differential thermal analysis and gravimetry. The
pozzolanic activity was measured according to the BNT NBR 12653(1997) norm. To evaluate the durability by the accelerate weathering (wetting and drying cycles) it was made body sample with conventional and alternative mortars with traces of 1:4; 1:6 e 1:8 incorporated with 3%, 6%, 9%,15%, 20% and 30% of ash rice husk residue in substitution of agglomerate and 10%, 20% and 30% of rice husk in substitution to small aggregate, for cure period of 28, 63, 91, 180 and 360 days. The physical and mechanical properties were: water absorption, apparent density,mechanical resistance and mass loss. The results of the conventional (cement and small aggregate) and alternative (ash and husk rice) raw materials characterization are in the standard values established by ABNT norms, indicating surface area and amount of fine particles of the husk rice ash are superior to the cement used. The results put in evidence that the husk rice ash is predominantly amorphous and has high pozzolanicity according to the specifications of the ABNT. This makes possible the use of this ash in concrete and mortars due to the great amount of fine particles. In relation to the mechanical properties, the results shown values superior to the body samples incorporated with husk rice in relation to the conventional even when exposed to the accelerate weathering. To the body samples incorporated with husk rice presented values according to the ABNT specifications and inferior to the conventional ones. It was concluded that the use of these residues are technical viable once did not present influence in the durability and also is an ecological correct action.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1902 |
| Date | 05 October 2018 |
| Creators | SOUZA, Jozilene de. |
| Contributors | NEVES, Gelmires de Araújo., FERREIRA, Heber Carlos., CARVALHO , João Batista Queiroz de., NASCIMENTO, José Wallace B. do., MENEZES , Romualdo Rodrigues., OLIVEIRA , Djane de Fátima., MOTA, Neusa Maria Bezerra. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds