Concrete has proven to be, by far, one of the most reliable materials for the construction of critical infrastructure. However, despite its structural capacity, concrete members are susceptible to damage mechanisms that may decrease its performance and durability throughout its service life. One such mechanism is alkali-silica reaction (ASR), which takes place when unstable siliceous phases present in coarse or fine aggregates react with the alkali hydroxides from the concrete pore solution, generating a secondary product (i.e., ASR gel); this product swells upon moisture uptake from the surrounding environment, leading to cracking and expansion of the affected concrete. In severe cases of ASR-affected infrastructure, structural safety could become a problem, and thus requiring the demolition of affected members. It is, therefore, necessary to adopt effective protocols for the diagnosis and prognosis of aging infrastructure, to ensure its performance over time along with properly planning for rehabilitation strategies, whether required. This work presents a two-stage case study of the S.I.T.E. building at the University of Ottawa for the diagnosis and prognosis of ASR-affected members (i.e., columns) after nearly 20 years in service. The diagnosis phase was conducted with the aim of evaluating the cause and extent of distress and interpreting its impact on the performance of the affected structure. First, a visual inspection was conducted to evaluate potentially damaged members, in order to select the best location for core-drilling. Once ASR was confirmed through petrographic examination, specimens were evaluated through the multi-level assessment (i.e., coupling of microscopic and mechanical assessment). A range of damage was discovered among the examined columns (i.e., 0.03%, 0.05%, and 0.08% expansion). Moreover, evidence of developing freeze and thaw (FT) damage was discovered in columns with greater levels of expansion, raising future concerns regarding the durability and serviceability of members affected by this coupling of damage (i.e., ASR+FT). For the second stage of this project (i.e., prognosis), a novel ASR semi-empirical model was developed with the aim of predicting future ASR-induced expansion and damage in the S.I.T.E. building. The above model was developed and validated (using ASR exposure site data) through the coupling of existing chemo-mechanical macro-models, which were used to predict material behaviour on the structural scale, and novel mathematical relationships for the prediction of anisotropy in the columns. Moreover, the use of the multi-level assessment to predict the mechanical implications of predicted distress was found to enhance the model’s capacity for prognosis and demonstrated important potential for the accurate prediction of multi-level damage in the S.I.T.E. columns.
| Identifer | oai:union.ndltd.org:uottawa.ca/oai:ruor.uottawa.ca:10393/42680 |
| Date | 16 September 2021 |
| Creators | Ahmed, Hesham |
| Contributors | Sanchez, Leandro |
| Publisher | Université d'Ottawa / University of Ottawa |
| Source Sets | Université d’Ottawa |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
Page generated in 0.0116 seconds