The cost of crystalline silicon solar cells must be reduced in order for photovoltaics to be widely accepted as an economically viable means of electricity generation and be used on a larger scale across the world. There are several ways to achieve cost reduction, such as using thinner silicon substrates, lowering the thermal budget of the processes, and improving the efficiency of solar cells. This thesis examines the use of plasma enhanced chemical vapour deposited silicon nitride to address the criteria of cost reduction for n-type crystalline silicon solar cells. It focuses on the surface passivation quality of silicon nitride on n-type silicon, and injection-level dependent lifetime data is used extensively in this thesis to evaluate the surface passivation quality of the silicon nitride films. The thesis covers several aspects, spanning from characterisation and modelling, to process development, to device integration. The thesis begins with a review on the advantages of using n-type silicon for solar cells applications, with some recent efficiency results on n-type silicon solar cells and a review on various interdigitated backside contact structures, and key results of surface passivation for n-type silicon solar cells. It then presents an analysis of the influence of various parasitic effects on lifetime data, highlighting how these parasitic effects could affect the results of experiments that use lifetime data extensively. A plasma enhanced chemical vapour deposition process for depositing silicon nitride films is developed to passivate both diffused and non-diffused surfaces for n-type silicon solar cells application. Photoluminescence imaging, lifetime measurements, and optical microscopy are used to assess the quality of the silicon nitride films. An open circuit voltage of 719 mV is measured on an n-type, 1 Ω.cm, FZ, voltage test structure that has direct passivation by silicon nitride. Dark saturation current densities of 5 to 15 fA/cm2 are achieved on SiN-passivated boron emitters that have sheet resistances ranging from 60 to 240 Ω/□ after thermal annealing. Using the process developed, a more profound study on surface passivation by silicon nitride is conducted, where the relationship between the surface passivation quality and the film composition is investigated. It is demonstrated that the silicon-nitrogen bond density is an important parameter to achieve good surface pas-sivation and thermal stability. With the developed process and deeper understanding on the surface passivation of silicon nitride, attempts of integrating the process into the fab-rication of all-SiN passivated n-type IBC solar cells and laser doped n-type IBC solar cells are presented. Some of the limitations, inter-relationships, requirements, and challenges of novel integration of SiN into these solar cell devices are identified. Finally, a novel metallisation scheme that takes advantages of the different etching and electroless plating properties of different PECVD SiN films is described, and a preliminary evalua-tion is presented. This metallisation scheme increases the metal finger width without increasing the metal contact area with the underlying silicon, and also enables optimal distance between point contacts for point contact solar cells. It is concluded in this thesis that plasma enhanced chemical vapour deposited silicon nitride is well-suited for n-type silicon solar cells.
Identifer | oai:union.ndltd.org:ADTP/257989 |
Date | January 2008 |
Creators | Chen, Wan Lam Florence, Photovoltaics & Renewable Energy Engineering, Faculty of Engineering, UNSW |
Publisher | Publisher:University of New South Wales. Photovoltaics & Renewable Energy Engineering |
Source Sets | Australiasian Digital Theses Program |
Language | English |
Detected Language | English |
Rights | http://unsworks.unsw.edu.au/copyright, http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0014 seconds