<p> A large focus of this thesis was developing the experimental procedures involved in imaging <i>VO<sub>2</sub></i> during the heating process. In order to study light interactions between an induced dipole and a sample surface to collect various data on its topography, amplitude and phase. Data is collected using a near-eld microscope (s-SNOM) and analyzed using various software that, normalize, lter and display the data in false color image. Specically, research behind this thesis, focuses on the phase transition of Vanadium Dioxide (<i>VO<sub>2</sub></i>) as it goes from an insulating to fully metallic phase. Using a wavelength of λ = 10:7<i>μm</i> to image the resonant behavior of the sample, the nucleation of <i>VO<sub>2</sub></i> was imaged as the temperature increased.</p>
| Identifer | oai:union.ndltd.org:PROQUEST/oai:pqdtoai.proquest.com:1600042 |
| Date | 24 October 2015 |
| Creators | Dunlap, Terrence L. |
| Publisher | California State University, Long Beach |
| Source Sets | ProQuest.com |
| Language | English |
| Detected Language | English |
| Type | thesis |
Page generated in 0.0017 seconds