A macro-photoluminescence study of self-catalyzed nanowires, using a specializedsetup for this purpose, has been performed. Several samples were even comparedto single nanowire micro-photoluminescence measurements, on the samesamples, done by other students in the nanowire group at NTNU. The macrophotoluminescence measurements were done by changing parameters such as temperature and excitation power. A 532 nm laser was used to excite the wires and thephotoluminescence was measured by a CCD detector attached to a spectroscope.Using macro-photoluminescence measurements in a qualitative comparison withmeasurements done on single nanowires by micro-photoluminescence spectroscopycan give the researcher a decent understanding of the quality of the sample and itscontributions to photoluminescence. Measurements done in this thesis show probablecontributions from most types of transitions expected in zinc-blende nanowires,consisting of such defects as dense zinc-blende/wurtzite heterostructures, highlytwinned regions, but also from nanowires of higher purity.As nanowires move closer to the realization of e.g. nanowire based solar cells,such macro-photoluminescence measurements will become increasingly importantin deciding the overall quality of the grown structures.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ntnu-18921 |
| Date | January 2012 |
| Creators | Slåttnes, Patrick Rene Tollefsen |
| Publisher | Norges teknisk-naturvitenskapelige universitet, Institutt for elektronikk og telekommunikasjon, Institutt for elektronikk og telekommunikasjon |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0218 seconds