Cimentos a base de resina metacrilato associado ao fosfato de cálcio : propriedades biológicas

Este trabalho teve como objetivo avaliar as propriedades biológicas de cimentos experimentais a base de resina metacrilato contendo α-tricálcio fosfato (α-TCP) ou hidroxiapatita nanoparticulada (HAp) in vitro e in vivo. Para isto, os cimentos experimentais foram avaliados e comparados com AH Plus (AHP). Na etapa in vitro, os materiais foram mantidos em contato com meio de cultura por 24 horas, coletados e avaliados na concentração de 10%. Células-tronco da papila apical humana (SCAPs) foram submetidas aos ensaios de viabilidade brometo de 3-(4,5-dimetiltiazólio)-2,5-difenil tetrazólio (MTT) e sulfurodamina B (SRB) no período de 24 horas; e a bioatividade foi avaliada pela atividade da enzima fosfatase alcalina (ALP) e deposição de nódulos mineralizados pelo corante vermelho de Alizarina (AR), nos períodos de 1, 5, 10 e 15 dias. Na etapa in vivo, os materiais foram inseridos em tubos de polietileno e colocados no tecido subcutâneo de ratos para avaliação da reação inflamatória, sendo utilizado um tubo vazio como controle e avaliados os períodos de 7, 30 e 90 dias; para avaliação da deposição óssea, os cimentos α-TCP e AHP foram inseridos em cavidades confeccionadas no fêmur de ratos, sendo utilizada uma cavidade vazia como controle e avaliados os períodos de 30 e 90 dias. Para o ensaio de viabilidade e ensaios in vivo, foram utilizados os testes de Kruskal-Wallis e post hoc de Dunn; para avaliação da bioatividade in vitro foram utilizados os testes ANOVA e post hoc de Tukey (P < 0.05). HAp e AHP não apresentaram diferenças estatísticas entre si em ambos os ensaios de citotoxicidade (P> 0,05) e o α-TCP apresentou menor resultado de viabilidade no teste MTT, sendo estatisticamente diferente dos outros (P <0,05). Os ensaios de bioatividade demonstraram aumento na atividade da ALP em todos os grupos (P < 0.05). Observou-se semelhança entre os grupos no primeiro período (P > 0.05), AHP apresentou menores valores em 5 dias (P < 0.05), α-TCP apresentou os maiores valores em 10 dias (P < 0.05), e em 15 dias este cimento foi superior ao AHP (P < 0.05). AR mostrou aumento na quantidade de depósitos mineralizados após 5 dias (P < 0.05). Não houve diferença entre os grupos em 1 dia (P > 0.05), α-TCP, HAp e controle foram semelhantes aos 5 dias (P > 0.05), e em 10 e 15 dias, α-TCP apresentou os maiores valores, sendo diferente dos outros cimentos (P > 0.05). Na avaliação da resposta inflamatória in vivo, observou-se diminuição da inflamação e aumento de fibras colágenas em todos os grupos. Em 7 dias, α-TCP e HAp mostraram resultados semelhantes ao controle CT (P>0.05) e diferentes do AHP (P < 0.05), que foi o único grupo a apresentar células-gigantes neste período. Na avaliação da deposição óssea, houve aumento na deposição de 30 para 90 dias nos grupos α-TCP e controle (P < 0.05), e estes grupos apresentaram resultados semelhantes em 90 dias (P > 0.05), diferindo do AHP (P < 0.05). Conclui-se que a associação de fosfatos de cálcio à resina metacrilato apresentou bons resultados de biocompatibilidade e bioatividade in vitro e in vivo, apresentando potencial para serem utilizados como cimentos obturadores na prática clínica. / This study aimed to evaluate the biological properties of experimental sealers containing α-tricalcium phosphate (α-TCP) or nanoparticulate hydroxyapatite (HAp) in a methacrylate resin-base in vitro and in vivo. For this, the experimental sealers were evaluated and compared with AH Plus (AHP). At the in vitro assays, the materials were kept in contact with culture medium for 24 hours, collected and evaluated at concentrations of 100% and 10%. Stem cells from human apical papilla (SCAPs) were submitted to 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) and sulfurodamine B (SRB) viability assays for 24 hour; and bioactivity was evaluated by alkaline phosphatase enzyme activity (ALP) and deposition of mineralized nodules by Alizarin Red staining (AR), for 1, 5, 10 and 15 days. At in vivo assays, the materials were inserted in polyethylene tubes and placed in subcutaneous tissue of rats to evaluate the inflammatory reaction, using an empty tube as control and evaluating the periods of 7, 30 and 90 days; to evaluate bone deposition, α-TCP and AHP cements were inserted into cavities made in the femur of rats, using an empty cavity as control and evaluating the periods of 30 and 90 days. For viability and in vivo assays, Kruskal-Wallis and Dunn’s post hoc tests were used; for bioactivity, ANOVA and Tukey's post hoc tests were used (P < 0.05). HAp and AHP did not presented statistical differences from each other in both citotoxicity assays (P > 0.05), and α-TCP presented a lower viability result in MTT assay, being statistically different from the other sealers (P < 0.05). The bioactivity assays showed an increase in ALP activity for all groups (P < 0.05). Similar results were found between the groups at the first period (P > 0.05), AHP had the lowest values at 5 days (P < 0.05), α-TCP presented the highest values at 10 days (P < 0.05), and at 15 days, this sealer’s values were higher than AHP (P < 0.05). AR showed an increase in the amount of mineralized deposits after 5 days for all sealers (P < 0.05). No difference between groups were found at 1 day (P > 0.05), α-TCP, HAp and control were similar at 5 days (P > 0.05), and at 10 and 15 days, α-TCP presented the highest values, being different of the other sealers (P > 0.05). Regarding the evaluation of the inflammatory response in vivo, there was a decrease in inflammation and increase of collagen fibers in all groups. At 7 days, α-TCP and HAp showed similar results to the control (P > 0.05) and different from AHP (P < 0.05), which was the only group to present giant cells in this period. In the evaluation of bone deposition, there was an increase in deposition from 30 to 90 days for α-TCP and control groups (P < 0.05), and these groups presented similar results in 90 days (P > 0.05), differing from the AHP (P < 0.05). It was concluded that the association of calcium phosphates and methacrylate resin showed good biocompatibility and bioactivity results in vitro and in vivo, presenting potential to be used as endodontic sealers in clinical practice.

Identiferoai:union.ndltd.org:IBICT/oai:www.lume.ufrgs.br:10183/173314
Date January 2017
CreatorsMestieri, Leticia Boldrin
ContributorsGrecca, Fabiana Soares
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFRGS, instname:Universidade Federal do Rio Grande do Sul, instacron:UFRGS
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds