A study is presented on the synthesis and characterization of nanoporous AgPt and AgAu
alloys after annealing and dealloying in 5% HClO4. Dealloying removes the less-noble atom
from the alloy surface to produce nanoporous, highly-interconnected ligaments. Voltammetry of AgPt and AgAu shows the critical potential, Ec, at various potential scan rates. Potential hold current decay experiments on Ag-23Pt and Ag-23Au further show the intrinsic Ec to be 275 mV and 290 mV, respectively. Ec was governed by thermodynamic clustering in the alloys as
opposed to dissolution-diffusion kinetic effects. EDX shows the starting 77Ag-23Pt material changes composition after dealloying to about 12Ag-88Pt. XRD indicates the presence of ordering in AgPt via a superlattice (100)-peak for a specific anneal treatment. EIS measurements done on as-annealed and dealloyed AgPt and AgAu samples show the onset of bulk porosity and show that capacitance increase is equal for both alloys at two different dealloying potentials.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/25594 |
| Date | 31 December 2010 |
| Creators | Ganti Mahapatruni, Aditya |
| Contributors | Newman, Roger C. |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0023 seconds