The presented diploma thesis deals with the potential use of colloidal silica in cement composites. Investigation is focused primarily on selected properties of cement pastes and mortars with colloidal silica content. Two selected types of colloidal silica (particles with average size of 14 nm) have been used as a cement addition and partial replacement of cement, respectively. The experimental program for cement pastes with colloidal silica included tests for isothermal calorimetry (the study of cement hydration) and thermal analysis (determining the portlandite content). Hardened cement pastes have been studied through measurements of compressive strength. The microstructure was examined by scanning electron microscopy. Hardened mortars with colloidal silica have been studied through measurements of compressive strength, flexural strength, modulus of elasticity and fracture mechanics parameters. Fracture mechanics tests show that 5 % and 20 % addition of colloidal silica can enhance after 28 days of curing fracture energy up to 18,4 % and 32,7 %, respectively. For the compressive strength enhancing effect of colloidal silica, it was found to be more pronounced in the early age, while rate of strength gain can be lower than the control in the later ages. Our investigations revealed that the silica sol will coagulate immediately when the cement is mixed into the water containing sol. The ionic composition of pore fluid significantly influences the stability of colloidal silica and lead to their aggregation. After additional tests it has been found that small addition of calcium hydroxide greatly improved the compressive strength of the resulting cement pastes with colloidal silica content. Addition of calcium hydroxide in conjunction with modified cement paste preparation can enhance compressive strength after 3 days of curing up to 64,4 % in comparison with the blank paste.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:240488 |
| Date | January 2016 |
| Creators | Barek, Jaroslav |
| Contributors | Žižková, Nikol, Rovnaníková, Pavla |
| Publisher | Vysoké učení technické v Brně. Fakulta stavební |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds