Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-10-16T14:58:40Z
No. of bitstreams: 1
HÉBERT RODRIGUES PEREIRA - DISSERTAÇÃO PPGEQ 2002..pdf: 21337764 bytes, checksum: b4876f987ec18ec26560a742ef52fa37 (MD5) / Made available in DSpace on 2018-10-16T14:58:40Z (GMT). No. of bitstreams: 1
HÉBERT RODRIGUES PEREIRA - DISSERTAÇÃO PPGEQ 2002..pdf: 21337764 bytes, checksum: b4876f987ec18ec26560a742ef52fa37 (MD5)
Previous issue date: 2002-02-18 / Capes / Na atual economia mundial globalizada, o Brasil se consolida como o maior mercado ocidental de revestimentos cerâmicos e como terceiro maior exportador mundial de revestimentos cerâmicos. Inserido neste cenário, o estado de Sergipe é hoje um dos pólos cerâmicos do país. Grande parte das argilas disponíveis no estado possui um elevado teor de carbonato de cálcio, que internacionalmente sofre restrições na sua utilização no processo de fabricação de revestimentos semiporosos e gressificados, por monoqueima rápida. O presente trabalho estudou composições de três argilas naturais
vermelhas com diferentes teores de carbonato de cálcio utilizados por uma unidade industrial do estado de Sergipe. Uma ampla caracterização destas argilas foi realizada tanto na forma de pó, quanto nos corpos cerâmico sinterizados, onde se evidenciou a influência da composição mineralógica no fenômeno de expansão por umidade. A aplicação da dilatometria se mostrou viável como ferramenta para o desenvolvimento de formulações cerâmicas a partir de argilas naturais. Outro aspecto evidenciado no estudo é que um aumento nos teores de carbonato na formulação da massa cerâmica proporciona uma diminuição da expansão por umidade à medida que favorece a formação de fases cristalinas de aluminossilicatos de cálcio e uma menor formação de fases vítreas. Foi também verificado o efeito de aditivos, pressão de compactação e ciclo de queima na identificação da melhor formulação para utilização industrial. Definiu-se então uma composição que atendeu as exigências das normas, possibilitando o emprego destas argilas calcificas no processo de fabricação, com um ciclo de queima muito rápido, o
que propiciará um forte retorno econômico para a unidade industrial. / In the world actual economy, Brazil appears as the biggest occidental market for ceramic tiles covers and as the third major world exporter of these products. Inserted in this scenery, the state of Sergipe is nowadays one of the ceramics polés of Brazil. A large quantity of available clay in Sergipe has a high percentage of calcium carbonate that is not well accepted in the manufacturing of semi porous and vitrified tiles covers, due to single fast firing. This report studied composition of three natural red clays with different rates of calcium carbonate used in one industrial plant in the state of Sergipe. A broad characterization of these clays has been made not only as a powdered shape but also as in the sinterized ceramics body, resulting the evidence of the influence of the mineralogical composition on the moisture expansion phenomena. The application of the dilatometer showed itself as a tool for the development of ceramics formulations based on the natural clays. Another aspect became evident on the studies, so as the increasing on the rates of carbonate in the ceramics mass provides a decrease in the moisture expansion while it enables the forming of crystalline phases of calcium aluminum silicates and a smaller formation of vitreous phase. Has been also observed that the effect of additives, compacting pressure and the firing cycle, during identification of the best formulation for industrial uses. Has been defined also a composition that attended the exigencies of normal standards, enabling the use of these calcites clays in the production process,
deriving a very short firing cycle, which will provide a strong economical return rate
for the industrial plant.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1978 |
| Date | 16 October 2018 |
| Creators | PEREIRA, Hébert Rodrigues. |
| Contributors | LIRA, Hélio de Lucena., FERREIRA, Heber Carlos., MELO, Aluísio Braz de., PASKOCIMAS, Carlos Alberto. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds