Nesse estudo, utilizamos a oleoresina de capsaicina, extraído da pimenta Malagueta (Capsicum frutensens) e da pimenta Dedo-de-moça (Capsicum baccatum), para a preservação de amostras de madeira contra o ataque do fungo Paecilomyces variotti. Os preservantes naturais foram aplicados em corpos de prova de madeiras do gênero Pinus sp. e Hymenae sp. (Jatobá) com as dimensões 5,0 x 3,0 x 1,0 (cm). A seguir, esses corpos de prova foram expostos ao fungo para o acompanhamento do seu desenvolvimento. As análises mostraram que o preservante natural retardou o crescimento do fungo, sendo a oleoresina de capsaicina extraído da pimenta Malagueta a mais eficiente se comparada à oleoresina extraída da pimenta Dedo-de-moça e ao óleo de linhaça. A partir da medida de ângulo de contato observou-se que o preservante de oleoresina da pimenta Malagueta proporcionava uma maior molhabilidade para as duas espécies de madeiras. A técnica de FTIR-ATR indicou que os preservantes não modificaram a estrutura das madeiras e a análise de raios X revelou que o desenvolvimento do fungo provocou uma perda de estabilidade e periodicidade nas estruturas das madeiras. Através do teste de proporção utilizado para a análise do desenvolvimento do fungo, comprovou-se estatisticamente que o seu crescimento foi menor para as amostras com os preservantes das pimentas. Pelo MEV foi possível visualizar as estrutura de hifas do fungo sobre a madeira. E a perda de massa para ambas as espécies de madeiras foram menores quando foram utilizados os preservantes, sendo o Pinus a espécie que sofreu maior degradação. / In this study, were used the oleoresin capsaicin, extracted from Capsicum frutensens and Capsicum baccatum, for the preservation of wood samples against the attack of the Paecilomyces variotti fungus. The natural preservatives were applied to Pinus sp. and Hymenaea sp. (Jatobá) specimens with the dimensions 5.0 x 3.0 x 1.0 (cm). Subsequently, these specimens were exposed to fungus and their development was monitored. . Analyses showed that the natural preservative slowed the growth of the fungus. Action of the oleoresin capsaicin extracted from Chilli pepper is the most efficient when compared to pepper oleoresin extracted from Capsicum frutensens and Capsicum baccatum and also with the linseed oil. The contact angle measured showed that the preservative of Oleoresin Chilli Pepper offered a higher wettability for both wood species. FTIR-ATR technique indicated that the preservatives did not change wood structure and X-ray analysis revealed that the development of the fungus caused a loss of stability and periodicity in the wood structures. At proportion test to analyze the development of the fungus, it was shown statistically that their growth was lower for the samples with preservatives peppers. It was possible to visualize the hyphae structure by scanning electronic microscopy technique. Mass loss of both wood specie was lower when preservative was used, and Pine species was more degraded.
| Identifer | oai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-16082010-143912 |
| Date | 20 July 2010 |
| Creators | Analine Crespo Ziglio |
| Contributors | Debora Goncalves, Carlito Calil Junior, Franciane Andrade de Pádua |
| Publisher | Universidade de São Paulo, Ciência e Engenharia de Materiais, USP, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds