Obtenção do compósito Nb-Cu via metalurgia do pó

Dissertação (mestrado)—Universidade de Brasília, Faculdade UnB Gama, Programa de Pós-graduação em Integridade de Materiais da Engenharia, 2016. / Submitted by Fernanda Percia França (fernandafranca@bce.unb.br) on 2016-12-23T15:06:00Z
No. of bitstreams: 1
2016_AndersonDiasMonteiro.pdf: 33676302 bytes, checksum: 226b42dc593cfbc51e37264c72a615cb (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2017-02-10T19:26:10Z (GMT) No. of bitstreams: 1
2016_AndersonDiasMonteiro.pdf: 33676302 bytes, checksum: 226b42dc593cfbc51e37264c72a615cb (MD5) / Made available in DSpace on 2017-02-10T19:26:10Z (GMT). No. of bitstreams: 1
2016_AndersonDiasMonteiro.pdf: 33676302 bytes, checksum: 226b42dc593cfbc51e37264c72a615cb (MD5) / O compósito Nb-Cu pode ser empregado na fabricação de contatos elétricos, resistências, eletrodos de solda, entre outros. Estes materiais devem apresentar elevadas condutividades elétrica e térmica e resistência ao calor. A produção desses compósitos pela tecnologia convencional é limitada, uma vez que envolvem elementos químicos que possuem pontos de fusão bastante diferentes. Uma alternativa é a adoção da metalurgia do pó. Desta forma, este trabalho tem como objetivo obter um compósito Nb-Cu via metalurgia do pó. Para isto, os pós de nióbio e cobre foram misturados nas proporções de 12,5% e 25%, respectivamente, em moinho planetário de bolas com base nos seguintes parâmetros: a razão bola/pó foi de 3:1; a velocidade de rotação, de 250 rpm; a atmosfera, vácuo; o agente controlador de processo, o estearato de zinco; e o tempo de moagem, de 2 horas e 8 horas. Em seguida, foram calculadas as densidades aparentes das misturas dos pós de nióbio e cobre. Em relação à compactação, esta foi feita em prensa universal, com aplicação de força de 3,2 x 104 N. Seguiu-se determinando a densidade dos compactados pelo método geométrico. Após a compactação, as amostras passaram por sinterização em forno tubular sob atmosfera de gás argônio a uma temperatura de 1000ºC para as amostras do lote 1 e 1100ºC para as amostras do lote 2, com isoterma de 1 hora em ambos os casos. A taxa de aquecimento e resfriamento foi de 5ºC/min. A densidade das amostras após a sinterização foi obtida através do método de Arquímedes. Os pós metálicos elementares, as misturas de pós metálicos moídos e os corpos sinterizados foram analisados via microscopia eletrônica de varredura e microscopia confocal. Medidas de DRX e microdureza (HV1) também foram realizadas. A partir destas análises, observou-se que o aumento do tempo de moagem torna as misturas de pós mais homogêneas e com partículas aglomeradas mais achatadas. Verificou-se, também, que as densidades aparentes das misturas de pós decrescem com o aumento do tempo de moagem, ao passo que os compactados à verde e os corpos de prova sinterizados têm suas densidades aumentadas com o aumento do tempo de moagem. Foi constatado, ainda, que a microdureza vickers têm seus valores aumentados tanto com o aumento do tempo de moagem quanto com o aumento da temperatura de sinterização. / The Nb-Cu composite can be used in the manufacture of electrical contacts, resistors, welding electrodes, among others. These materials should have high electrical and thermal conductivities and heat resistance. The production of these composites is limited by the conventional technology, as they involve chemicals that have very different melting points. An alternative is the use of powder metallurgy. Thus, this study aims to obtain a Nb-Cu composite via powder metallurgy. For this, the niobium powders and copper were mixed in the proportions of 12.5% and 25%, respectively, in a planetary ball mill using the following parameters: the ratio ball / powder was 3: 1; rotation speed of 250 rpm; atmosphere, vacuum; the agent process controller, zinc stearate; and the grinding time of 2 hours and 8 hours. Then, the apparent densities of the mixtures of niobium powders and copper were calculated. In relation to the compaction, it was done in the universal press with force applying 3.2 x 104 N. This was followed by determining the density of compressed by geometrical method. After compaction, the samples underwent sintering in a tubular furnace under an atmosphere of argon gas at a temperature of 1000 ° C for samples 1 and 1100ºC batch to batch of samples 2, with 1 minute isotherm in both cases. The heating and cooling rate was 5 ° C / min. The density of the samples after sintering was obtained by the Archimedes method. The elemental metal powders, metal powder mixtures milled and sintered bodies were analyzed via scanning electron microscopy and confocal microscopy. XRD measurements and hardness (HV1) were also performed. From these analyzes, it was observed that increasing milling time becomes more homogeneous mixtures of powders and agglomerated particles flatter. It was found also that the apparent density of the powder mixtures decreased with increased milling time while the green compacted and sintered specimens have their densities increased with increasing milling time. It has been found, furthermore, that the Vickers microhardness values both have their increased with increasing milling time and with increasing the sintering temperature.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/22467
Date22 August 2016
CreatorsMonteiro, Anderson Dias
ContributorsMuterlle, Palloma Vieira
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB
RightsA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess

Page generated in 0.002 seconds