This study aims to experimentally explore the possibility to join the two pieces of low-carbon steel and Cu-Ni alloy as the cladding material into a thick clad steel plate during a Friction Stir Lap Welding¡]FSLW¡^process without a probe. Two methods are employed to enhance the welding strength. Firstly, a layer of nickel is coated on the low-carbon steel to prevent it from oxidizing during the welding process. Secondly, the surface of the low-carbon steel is knurled to increase the contact area between the welding surfaces.
Experimental results show that Ni-coating can effectively prevent the generation of oxidation and improve the welding strength. According to the tensile test using a plate of Cu-Ni alloy with a thickness of 4 mm, the welding strength of the clad steel plate with Ni-coating is about 2.3 times greater than that without Ni-coating. Moreover, according to the impact test, the clad steel plate with Ni-coating can absorb more impact energy than that without Ni-coating. This difference increases with increasing thickness of the plate. It is also found that the welding strength at the center of joints using the Ni-coating is greater than that at the substrate of copper-nickel alloy. For the clad steel plate with knurling, since it is difficult to fill the gap between the patterns of knurling, the increase in the contact area between the welding surfaces has been offset. Hence, the welding strength of the clad steel plate with knurling is less than that with Ni-coating.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0824109-181510 |
| Date | 24 August 2009 |
| Creators | Sung, Cheng-Chang |
| Contributors | Rong-Tsong Lee, Li-ming Chu, Yuang-Cherng Chiou, Yuh-Ping Chang, Chung-Ming Lin |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0824109-181510 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0011 seconds