Many industries including the medical, aerospace, and automobile industries have increasingly adopted the use of shape memory alloys (SMAs) for a plethora of applications due to their unique thermomechanical properties. From the commercially available SMAs in the market, binary NiTi SMAs have shown the most desirable properties. However, SMA properties can be significantly affected by the fabrication process. One of the most familiar applications of NiTi SMAs is in the design of actuating devices where the shape memory effect properties are highly advantageous. Spring NiTi SMA actuators are among the most commonly used and are generally made by torsion loading a straight wire. Consequently, stress concentrations are formed causing a reduction in recovery force. Other methods for producing springs and other NiTi SMA components is the fast emerging manufacturing method of additive manufacturing (AM). AM often uses metal powders to produce the near-net shape components. A major challenge for SMAs, in particular, is their well-known composition sensitivity. Therefore, it is critical to control composition in NiTi SMAs. In this thesis, a novel method for processing NiTi SMAs for pre-alloyed NiTi SMA powders and springs is presented. A low pressure and low temperature hydriding-pulverization-dehydriding method is used for preparing the pre-alloyed NiTi SMA powders with well-controlled compositions, size, and size distributions from wires. By hydrogen charging as-drawn martensitic NiTi SMA wires in a heated H3PO4 solution, pulverizing, and dehydriding, pre-alloyed NiTi powders of various well-controlled sizes are produced. In addition, a low pressure and low temperature hydriding-dehydriding method is used for producing NiTi SMA helixes from wires. The helix pattern in the pre-alloyed NiTi SMA wires was obtained by hydrogen charging NiTi SMA 500 μm diameter wires at different time intervals, followed by dehydriding to remove the hydrogen. The wires, powders, and resulting helixes were characterized using scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and x-ray diffraction (XRD). The relationship between the wire diameter, powder particle size, and helix geometry as a function of hydrogen charging time is investigated. Lastly, the recovery behavior due to the shape memory effect is also investigated after dehydriding.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc1157656 |
Date | 05 1900 |
Creators | Briseno Murguia, Silvia |
Contributors | Young, Marcus L., Mishra, Rajiv, Aouadi, Samir |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | ix, 70 pages, Text |
Rights | Public, Briseno Murguia, Silvia, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0033 seconds