Thesis (MTech (Mechanical Engineering))--Cape Peninsula University of Technology, 2010. / Hybrid polymeric composites (HPC) are widely used for the design of aerospace, automobile and civil engineering structures. One of the major challenges posed by these materials and structures is their brittle nature. When subjected to impact and dynamic loads, the polymeric composite structures undergo micro cracking. The cracks coalesce, propagate and can lead to catastrophic failure of the material and structures.
In this thesis, an intelligent hybrid polymeric composite (IHPC) beam with healing ability was developed and tested. The IHPC beam developed consisted of a 3% prestrained 1mm diameter Ni-Ti shape memory alloy (SMA) wire actuator embedded in the polymeric host matrix. The function of the embedded Ni-Ti shape memory alloy was to enhance intelligence and healing ability to the IHPC beam.
Upon electric current resistance heating, the Ni-Ti SMA actuator responds by contracting as a result of detwinned martensite → austenite phase transformation. Contraction of the SMA in the IHPC beam was utilized to stiffen and enhance healing by retarding crack growth and recovery of the strain induced in the loaded IHPC beam. This can result to increase of the flexural stiffness EI (defined as the product of the Young’s Modulus E of the material and the moment of inertia I of the geometry of the beam) and mode I fracture stress intensity factor KIC of the IHPC beam.
One (1) mm diameter Ni-Ti SMA wire was used in the experimental work in this thesis. The wire was cut into 35 pieces, 200 mm long each. Ni-Ti SMA wires were heated in the furnace to a temperature of 250ºC for ten (10) hours then were left to cool in the ambient air. The heat treatment was aimed to release any residual stress and to stabilize the austenite start (AS) and austenite finish (Af) transformation temperatures of the Ni-Ti SMA.
After heat treatment, the Ni-Ti SMA wires were prestrained by 3% (based on a gauge length of 150mm) on a tensile testing machine. Prestraining of the Ni-Ti SMA wires was aimed to induce detwinned martensite volume fraction in them hence increasing the transformation strain and recovery force of the Ni-Ti SMA actuator.
Intelligent hybrid polymeric composite (IHPC) beams and polymeric virgin (PV) beams, all of dimensions 150mmx25mmx10mm were manufactured by casting 60D polyurethane thermosetting epoxy resin in a silicon mould. transformation strain and recovery force of the Ni-Ti SMA actuator.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:cput/oai:localhost:20.500.11838/1251 |
Date | January 2010 |
Creators | Mwita, Wambura Mwiryenyi |
Publisher | Cape Peninsula University of Technology |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis |
Rights | http://creativecommons.org/licenses/by-nc-sa/3.0/za/ |
Page generated in 0.0019 seconds