This diploma thesis is focused to nickel coatings on magnesium alloys. At the introduction of this work is briefly commented phase composition of AZ91 alloy, which is followed by detailed description of five very different theories of Ni-P coatings formation. Theoretical part is ended by review aimed to current states of development in areas of chemical nickel coating, influence of AZ91 alloy microstructure to current less deposition and possibility of surfactants influence to decrease of surface roughness. In experimental part of this thesis was the morphology and composition of Ni-P coatings including interlayers dependence on chemical composition of nickel-plating bath and magnesium alloy surface pre-treatment investigated using scanning electron microscopy and inverted optical microscopy. Average phosphorus content was obtained using energy dispersive analysis. Closing part of experimental part was dedicated for mechanical properties of coatings by micro-indentation analysis.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216994 |
| Date | January 2013 |
| Creators | Kosár, Petr |
| Contributors | Richtera, Lukáš, Zmrzlý, Martin |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.006 seconds