M. Tech. Metallurgical Engineering / Mild steel is vulnerable to corrosion; this behaviour affects the material strength and electrochemical behaviour during industrial application. Mild steel also has poor tribological resistance; its application for the components of machines, however, requires good tribological property. The cost incurred from equipment failures, properties loss and increased production overheads makes is imperative to enhance mild steel's electrochemical and tribological properties. Electroless nickel plating has found extensive use in various industries attesting to its exceptional properties. The effect of bath parameters on the electroless plating process is of importance as this affects the adhesion, morphological behaviour, electrochemical properties and uniformity of coating. The key aim of this research is: To generally improve the understanding of the effect of electroless binary and ternary alloys on the corrosion and wear resistance of mild steel using weight loss method, potential measurement, linear polarization and tribological sliding wear tests. This work studies the effect of temperature, concentration, deposition time and the inclusion of Tin (Sn) as a third addition to the electroless bath. Corrosion and wear behaviour of the electroless plated mild steel was studied.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:tut/oai:encore.tut.ac.za:d1001526 |
| Date | January 2014 |
| Creators | Osifuye, Onosetalese Christiana. |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Text |
| Format |
Page generated in 0.0022 seconds