An investigation of precipitation was carried out on the system Cu-Ni-Co at temperatures varying from 600°C to 800°C over a wide range of composition . The precipitation process was studied primarily by use of X-ray diffraction techniques.
The precipitation was observed to procede by a spinodal decomposition
process. The initial wavelength of the modulated structure
was in the range 40 to 55Å, in good agreement with the theory for spinodal decomposition. On ageing, a coarsening was observed for all alloys aged inside the spinodal. This coarsening appeared to follow a law of the form
Q[superscript: m] – Qo[superscript: m] = k (t-to) where Q = wavelength at time t
Qo = wavelength before the coarsening begins at time to k and m = constants
The activation energy of the coarsening process was found to be 65 kcal/mole + 10 kcal suggesting that volume diffusion was the controlling factor.
RESUME
Le présent travail étudie la formation de précipités dans divers alliages du systéme Cu-Ni-Co au cours de vieillissements à des temperatures de 600°C a 800°C. L’évolution de la précipitation a été suivie principalement par diffraction des rayons X.
On a observé que la précipitation procède par décomposition spinodale. La longeur d'onde initiale de la structure modulée est comprise
entre 40 et 55Å; en bon accord avec la théorie de la décomposition spinodale de Cahn. Au cours du vieillissement on a mesuré un accroissement de la longeur d'onde pourtous les alliages traités à l'intérieur du spinodal. Cet accroissement de longeur d'onde obéit à une loi de la forme
Q[superscript: m] – Qo[superscript: m] = k (t-to)
ou Q = longeur d'onde au temps t
Qo = longeur d’onde avant que le grossisement commence, à to
k et m = constantes if energie d'activation du mécanisme de croissance des précipités a été déterminée; sa valeur, 65 kcal/mole suggére que la diffusion en volume est le facteur préponderant. / Applied Science, Faculty of / Materials Engineering, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/36360 |
| Date | January 1967 |
| Creators | Vandermousen, Roland F. |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | French |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0021 seconds