Nickel-base superalloys have been emerged as materials for gas turbines used for jet propulsion and electricity generation. The strength of the superalloys depends mainly from an ordered precipitates of L12 structure, so called gamma prime (γ’) dispersed within the disorder γ matrix. The Ni-base alloys investigated in this dissertation comprise both model alloy systems based on Ni-Al-Cr and Ni-Al-Co as well as the commercial alloy Rene N5. Classical nucleation and growth mechanism dominates the γ’ precipitation process in slowed-cooled Ni-Al-Cr alloys. The effect of Al and Cr additions on γ’ precipitate size distribution as well as morphological and compositional development of γ’ precipitates were characterized by coupling transmission electron microscopy (TEM) and 3D atom probe (3DAP) techniques. Rapid quenching Ni-Al-Cr alloy experiences a non-classical precipitation mechanism. Structural evolution of the γ’ precipitates formed and subsequent isothermal annealing at 600 °C were investigated by coupling TEM and synchrotron-based high-energy x-ray diffraction (XRD). Compositional evolution of the non-classically formed γ’ precipitates was determined by 3DAP and Langer, Bar-on and Miller (LBM) method. Besides homogeneous nucleation, the mechanism of heterogeneous γ’ precipitation involving a discontinuous precipitation mechanism, as a function of temperature, was the primary focus of study in case of the Ni-Al-Co alloy. This investigation coupled SEM, SEM-EBSD, TEM and 3DAP techniques. Lastly, solute partitioning and enrichment of minor refractory elements across/at the γ/ γ’ interfaces in the commercially used single crystal Rene N5 superalloy was investigated by using an advantage of nano-scale composition investigation of 3DAP technique.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc700080 |
Date | 08 1900 |
Creators | Rojhirunsakool, Tanaporn |
Contributors | Banerjee, Rajarshi, Collins, Peter (Peter C.), Srivilliputhur, Srinivasan Gopalan, Williams, James, Needleman, A. |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | xi, 153 pages : illustrations (some color), Text |
Rights | Public, Rojhirunsakool, Tanaporn, Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0083 seconds