The thesis is focused on clarifying fatigue damage mechanisms and fatigue-creep damage mechanisms of MAR-M 247 and IN 713LC polycrystalline Ni-based superalloys. This thesis begins with basic information about nickel-based superalloys and their microstructure, followed by a description of fatigue and creep mechanisms and their mutual interaction. The next part contains experimentally obtained results describing the behavior of MAR-M 247 and IN 713LC superalloys under various sets of conditions. Three testing temperatures - 800, 900 and 950 °C were used for the measurement of fatigue properties under symmetrical loading cycle, because in the temperature range 800 – 950 °C, the mechanism of fatigue crack propagation of both superalloys should change from the originally crystallographic at "lower" temperatures (800 °C) to non-crystallographic at "higher" temperatures (950 °C). In addition the effect of processing technology on fatigue properties was studied on the superalloy IN 713LC. High-frequency cyclic loading (about 120 Hz) with high mean stress at elevated temperatures was applied to induce fatigue-creep interaction. The combined fatigue-creep loading was performed on the IN 713LC superalloy at 800 °C and on the MAR-M 247 superalloy at 900 °C.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:433626 |
| Date | January 2021 |
| Creators | Horník, Vít |
| Contributors | Kohout, Jan, Pantělejev, Libor, Kunz, Ludvík |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0057 seconds