Leaching is the most widely used process for extraction of nickel metal from lateritic ores.
In this study, nickel extraction from Manisa-Gö / rdes region laterites by hydrochloric acid leaching is aimed. The mineralogical analysis of sample showed that hematite, goethite, dolomite, quartz and smectite are the main minerals in the ore. Attrition scrubbing, cycloning and magnetic separation with permroll were used as preconcentration processes but results were unsatisfactory. HCl leaching experiments were conducted both at room temperature and at elevated temperatures. The effects of various parameters such as leaching duration, particle size, concentration of HCl, pulp density, Cl- concentration and temperature on nickel recovery were examined. The results showed that under the optimised leaching conditions (particle size: 100 % -1 mm, HCl concentration: 3 N, leaching duration: 3 hours, leaching temperature: 100 oC, pulp density: 1/30 solid to liquid ratio by volume) it was possible to extract 87.26 % of nickel in the ore.
Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12607738/index.pdf |
Date | 01 September 2006 |
Creators | Goveli, Ahmet |
Contributors | Atalay, Umit Mustafa |
Publisher | METU |
Source Sets | Middle East Technical Univ. |
Language | English |
Detected Language | English |
Type | M.S. Thesis |
Format | text/pdf |
Rights | To liberate the content for public access |
Page generated in 0.002 seconds